In order to investigate the effect of irradiation by 60Co-γrays as well as the e thermal treatment on the dielectric deterioration in ethylene propylene rubber, insulating material for electric cables used in atomic power plants, charging discharging current, residual built- up voltage and dielectric properties are measu discussed in this study. Variance in the characteristic of relative dielectric constant as a function of tem was observed in relatively high dose of irradiation. Since glass transition tem appeared at tens of degree Celsius below zero, the characteristic is attributed orientation polarization. Dielectric loss is generally increased, with increasing d irradiation in the characteristic of dielectric loss as a function of temperature, No d loss by thermal treatment was observed. Dielectric resistance decreases with increa of irradiation in the characteristic of charging current as a function of temperature be considered that dielectric resistance seems to be recovered by thermal treatm characteristic of discharging current as a function of time in the specimen less ir become similar to that of the unirradiated, when thermal treated. A peak is shown residual built- up voltage as a function of time, and the corresponding time of the shorten as increasing dose of irradiation. It is also observed that the corresponding the peak is lengthened by thermal treatment.

직물의 태는 손으로 만져 보았을 때 느껴지는 감촉, 육안으로 느껴지는 감각, 그리고 직물의 물리적 역학적 성질 등이 함께 어울어져 이루어지는 것이다. 따라서 본 연구에서는 폴리에스테르 원형사와 삼각사로 제직된 직물의 태와 온/냉감 및 광택도를 측정하였다. 삼각단면사로 제직된 직물이 원형단면사로 제직된 직물보다 더 좋은 태를 보였으며 열전달계수가 크게 나타나 냉감을 느낄 수 있었으며 높은 반사율을 보였다.

Part I에서 도출된 기초 식을 적용하여 입자 분산 강화형, 섬유 강화형 및 적층형 복합재료의 유효탄성제수 및 열팽창계수를 산정 하였다. 일방향 섬유 강화 복합재료의 경우 섬유의 유효 축비 (aspect ratio)가 고려되었으며, 유효 탄성계수는 다른 연구 결과들과 비교하였다. 입자 분산 강화형 복합재료의 유효 체적탄성률 및 전단 탄성률은 Korner의 표식 및 Hanshin과 Shtrikman의 하한치 (lower bounds)와 일치하고 있다. 일방향 섬유 강화 복합재료에서는 6개, Hanshin과 Rosen의 모델에 나타낸 4개의 독립 탄성계수와 일치하고 있다.

급냉응고방식으로 제조한 비정질 Z r62-xN i10C u20A l8 Tix (x=3, 6, 9at%) 합금을 사용하여 열적, 기계적 성질을 조사하였다. 시효온도에 따른 결정화 거동은 Ti 3at%에서는 비정질→비정질+Z r2A l3+Zr+(Ni,Ti)→Z r2Cu+Al+(Ni,Ti)의 결정화 거동을 나타내었으며, Ti 6at%에서는 비정질→비정질+Al→A l2Ti+NiZr+CuTi, Ti 9at%에서는 비정질→비정질+Zr+Al→Zr+A l2Zr+Al Ti3+CuTi의 결정화 거동을 보였다. 시효온도가 증가할수록 비정질 모상에 석출상의 체적율( Vf )이 증가하고 그에 따라 비커스 경도 ( Hv )간이 증가하였다. 파괴인장강도(σf )는 Vf 의 증가에 따라 증가하다가 Z r59A l10N i20C u8 Ti3은 Vf =38%에서 1219MPa의 최대값을 보이고, Z r56A l10N i20C u8 Ti6은 Vf =2%에서 1203MPa의 최대값을 보이고, Z r53A l10N i20C u8 Ti9 Vf =5%에서 1350MPa의 최대값을 나타낸 후 그 이상의 Vf 에서는 급격히 감소하였다. σf 가 급격히 감소하는 Vf 와 연성 파면에서 취성파면으로 천이되는 Vf 가 일치하였다.f/가 일치하였다.

In order to enhance sinterability of W-Cu composites used for heat sink materials, mechanical alloying process where both homogeneous mixing of component powders and fine dispersion of minor phase can be easily attained was employed. Nanostructured W-Cu powders prepared by mechanical alloying showed W grain size ranged of 20-50 nm and were able to be efficiently sintered owing to the fine particle size as well as uniform distribution of Cu phase. The thermal properties such as electrical resistivity, coefficient of thermal expansion and thermal conductivity were evaluated as functions of temperature and Cu content. It was found that the coefficient of thermal expansion could be controlled by changing Cu content. The measured electrical resistivities and thermal diffusivities were also varied with Cu content. The thermal conductivities calculated from the values of resistivities and diffusivities showed similar tendency as a function of temperatures. However, this is in contradiction with thermal conductivities of pure W and Cu which decrease with increasing temperature.

자동차, 항공기 및 기타 산업에서 복합재료의 사용은 증가되어 왔고 활발한 연구가 진행되고 있다. 이러한 복합재료중의 하나인 carbon-epoxy 복합재료의 열 특성에 관하여 알아보았다. 반복적인 냉각과 가열이 부가된 후 복합재료의 탄성계수의 변화를 관찰하여 봄으로써 복합재료가 가지고 있는 여러 열 특성에 관하여 여러 열 특성에 관하여 연구하였다. 이 연구에서는 G(sub)13값은 약한 감소하기는 하였으나 별다른 변화를 보이지 않았으며 열충격의 경우가 열피로의 경우보다 변화량이 작았다. E1값은 가해진 온도와 가열 횟수에 따라하여 조금씩 증가하였고, E2, G(sub)23값은 열피로의 경우 처음에는 어느 정도 그 값이 감소하나 가해진 횟수에는 큰 영향을 받지 않았으며 열충격의 경우에는 온도에 따라 다른 현상을 보였다.

가용성 폴리이마드 주쇄에 Disperse-Red 1 크로모포를 공유결합 시킨 옆사술계 비선형 전기광학 고분자를 합성하였다. 합성된 고분자의 유리전이온도 빛 열분해온도 는 각각 225˚C, 310˚C이었으며 광통신 파장에서 광학적으로 투명하였다. 100 V/μm의 전기장으로 폴링했을 때, 유전상수는 10 kHz에서 3.37이며, 파장 1300 nm에서, 굴절률은 nTE 및 nTM 모두 1.631로같았으며, 전기광학계수는 4.6 ~ 9.2 pm/V이였다. 폴링한 후 180˚C에서 1시간 동안 유지시킨 시편의 전기광학계수의 값은 감소되지 않 았으며, 장기적인 관점에서 90˚C에서 500 시간 동안 유지시킨 시편의 전기광학계수도 변함이 없었다.

파장분할다중 광소자용으로 새로운 치환된 고분자인 폴리아릴렌에테르를 합성하였다. 이 물질은 열적으로 500˚C까지 안정하며, 1.5μm의 파장 근처에서 넓은 투과 영역을 가진다. 굴절률도 1.495-1.530의범위에서 불소 함유량으로 조절되었다. 단일 모드 광도파로를 제작하여 광도파손실을 측정하였다. 측정된 광도파손실은 1.55μm의 파장에서 0.2 dB/cm 이하였다.

저밀도 에너지를 효율적으로 축열하기 위해서 현열축열재보다는 상변화 온도 30℃ 수준의 잠열축열재를 이용하는 것이 효과적이다. 이를 위하여 연구를 수행한 결과, SCD에 APS를 0.0~5.0wt% 첨가하여 과냉도를 25.0℃에서 1.5℃ 이하로 조절하였으며, APS의 적정 함량은 3.0wt%였다. SCD에 PSC를 0.0~3.0wt% 첨가하여 상분리량을 70.0%에서 0.0%로 조절하였으며, PSC의 적정 함량은 1.5wt%였다. 축열재 내구성 검증을 위하여 0~1,500회의 상변화 사이클을 수행한 결과 상변화 온도의 변화량이 30±l.0℃ 이하, 잠열량 변화가 54±2.0 Kcal .kg-1 이하로 안정된 값을 보였다. 따라서 축열재의 수명은 10년 정도 보장될 수 있는 것으로 판단되었다