Nanostructured Cu-AlO composite powders were synthesized by thermochemical process. The synthesis procedures are 1) preparation of precursor powder by spray drying of solution made from water-soluble copper and aluminum nitrates, 2) air heat treatments to evaporate volatile components in the precursor powder and synthesis of nano-structured CuO + O, and 3) CuO reduction by hydrogen into pure Cu. The suggested procedures stimulated the formation of the gamma-AlO, and different alumina formation behaviors appeared with various heat treating temperatures. The mean particle size of the final Cu/AlO composite powders produced was 20 nm, and the electrical conductivity and hardness in the hot-extruded bulk were competitive with Cu/AlO composite by the conventional internal oxidation process

All-vanadium redox flow battery(VRFB) has been studied actively as one of the most promising electrochemical energy storage systems for a wide range of applications such as electric vehicles, photovoltaic arrays, and excess power generated by electric power plants at night time. CPCS has been shown to have the characteristics as an excellent current collector for VRFB and electrochemical properties of specific resistivity 0.31 Ω cm, which were composed of G-1028 80 wt%, PVC 10 wt%, DBP 5 wt% and FS 5 wt%. Energy efficiencies of VRFB with the CPCE and the existing electrode assembly were 84.14 % and 77.24 % respectively, in charge/discharge experiments at constant current of 200 mA, and the CPCE was confirmed to be suitable as the electrode of VRFB.

In the electrode fabrication of unit cell, we found that optimal the electrochemical characteristics were obtained with at 90 wt.% of activated carbon(BP-20), 5 wt.% of conducting agent(Ppy, Super P) and 5 wt.% of P(VdF-co-HFP)/PVP mixed binder. The electrochemical characteristics of unit cell with Ppy improver were as follows : 37.6 F/g of specific capacitance, 0.98 Ω of AC-ESR, 2.92 Wh/kg and 6.05 Wh/L of energy density, and 754 W/kg and 1,562 W/L of power density. It was confirmed that internal resistance were reduced due to the increase of electrical conductivity and filling density by the introduction of conductivity agent, and content of conducting agent was suitable in the range of 4~6 wt.%. According to the impedance measurement of the electrode with conductivity agent, we found that it was possible to charge rapidly by the fast steady-state current convergence due to low equivalent series resistance(AC-ESR), fast charge transfer rate at interface between electrode and electrolyte, and low RC time constant.

The electrochemical behavior of the LiCoO2 electrode, containing carbon black as a conductor, depends upon the nature and characteristics of carbon black. In this study, six different kinds of carbon blacks were employed to investigate the relationship between the properties of carbon blacks and electrochemical characteristics of the electrode. The larger amount of surface oxygen functional groups brought the lower electrical conductivity for the carbon blacks. The electrical conductivity of carbon blacks was closely related to the impurities such as ash and volatile content. The rate capability and cyclability of the electrode were improved with the higher conductivity of carbon blacks used. So, it can be concluded that high conductive carbon black plays an important role as a conductor for high rate of charge-discharge capability and initial efficiency.

코발트 산화물 박막을 전극으로 하여 Pt/Ti/Si 기판위에 Co3O4/LiPON/Co3O4로 구성된 전고상의 박막형 슈퍼캐패시터를 제작하였다. 각각의 Co3O4박막은 반응성 dc 마그네트론 스퍼터를 이용하여 O2/[Ar+O2] 비를 증가 시키며 성장시켰고, 비정질 LiPON 고체전해질 박막은 순수한 질소분위기 하에서 rf 스퍼터링으로 성장시켰다. 비록 벌크 타입의 슈퍼캐패시터에 비해 낮은 전기용량 (5-25mF/cm2-μm)을 가졌지만, Co3O4/LiPON/Co3O4 구조로 제작된 전고상 박막형 슈퍼캐패시터는 벌크 타입과 비슷한 거동을 나타내었다 0-2V의 전압구간, 50μA/cm2의 전류밀도에서 약 400사이클 까지 안정한 방전용량을 유지함을 관찰할 수 있었다 이러한 전고상 박막형 슈퍼캐패시터의 전기화학적 특성은 O2/[Ar+O2] 비에 의존하는데, 이러한 의존성을 구조적, 전기적 특성 및 표면특성을 분석하여 설명하였다.

PDP용 투명유전체 재료로 사용되는 PbO-B2O3-SiO2-Al2O3계의 소성과정 중에서 투명전극 (ITO)과의 반응성 및 광학적, 열적, 전기적 특성을 조사하였다. 본 연구에서 유전체막.두께는 12μm으로, 온도는 550-580˚C에서 소성한 후 여러 물성을 평가하였다 그 결과로, 유전체와 투명전극(ITO)의 반용에서, In 이온이 유전체층으로 확산이동하였으며, Sn 확산은 거의 발생하지 않았다. 선팽창계수, 유전상수, 유리전이온도,광 투과율은 유전체 조성의 PbO 양에 큰 영향을 받았다. PbO양 증가는 선팽창계수와 유전상수를 증가시킨 반면, 유리전이온도와 광 투과율온 저하시켰다. Al2O3/B2O3 비가 증가함에 따라서는 선팽창계수는 감소, 유전상수는 증가, 광 투과율은 감소하였으며, 유리 전이점 변화는 거의 나타나지 않았다.

고분자전해질형 연료전지에서 촉매의 활성을 증가시키기 위하여 기존에 사용되고 있는 백금과 전이금속인 chromium, nickel과의 합금을 제조하였다. XRD를 이용하여 합금의 구조가 33˚에서 superlattice line을 가지고 있는 것으로 보아 face centered cubic 구조를 가진 ordered alloy로 이루어졌다는 것을 알 수 있었다. 열처리 온도가 증가할수록 합금의 입자 크기는 증가하였으며, 결정 격자 상수는 감소하였다. 전지성능테스트, cyclic voltammogram 등을 통하여 mass activity, specific activity, Tafel slope, 개회로 전압을 측정한 결과, 합금촉매의 활성이 순수한 백금촉매보다 크게 향상되었음을 알 수 있었다.

Metal-Ferroelectric-Metal(MFM) 구조의 개퍼시터에서 Pb(Zr,Ti)O3(PZT)-전극 계면층이 PZT 박막 특성에 기여하는 영향을 알아보기 위하여 Pt/PZT/계면층/Pt/TiO2/SiO2/Si 구조의 캐퍼시터를 제작하였다. 계면층으로 사용될 물질들 중에서 PbTiO3(PT) 층을 sol-gel 방법으로 형성하였으며, PbO, ZrO2, TiO2 층들을 reactive sputtering 방법으로 형성하였다. PZT박막을 구성하는 원소들로 이루어진 단순 산화물들의 특성을 평가하기 위하여 PbO, ZrO2, TiO2를 계면층으로 사용하여 600˚C에서 열처리를 실시하였고, 이 경우에는 TiO2가 가장 우수하게 PZT의 결정립 크기를 미세하게 하는 효과를 보였으나, 두께가 증가함에 따라 표면 거칠기가 증가하고 anatase 상으로 남기 때문에 강유전특성이 열화되었다. 반면에 PT 박막을 계면층으로 사용한 경우에는 결정립 크기의 감소와 더불어 전기적인 특성도 향상되었다. 또한 PZT의 핵생성 위치를 판단하기 위하여 PT 삽입층의 위치를 변화하며, 실험한 결과, 하부전극과 PZT 박막의 계면에 PT 삽입층을 형성하였을 경우에 가장 효과적인 seed로서의 역할을 하였다.

Performance of direct methanol fuel cell using high porous active carbon as an uncatalysed diffusion layer in anode (composite electrode) has been evaluated. Effects of porous active carbon in anode were investigated by galvanostatic method and Fourier Transform Infrared spectroscopy. The single cell was operated with 2.5 M methanol at temperature of 80-120℃ and showed performance of 210-510 mA/cm2 at 0.4V. By replacing conventional electrode with composite electrode, the increment of 290 mA/cm2 in current density was obtained at 90℃and 0.4V. The potential decay of the single cell was about 14.5% for 20 days operation.

Electrochemical charateristics of activated carbon fiber cloth(ACFC) electrode were studied with propylene carbonate(PC), γ-butyrolactone(GBL) and N,N-dimethyl-formamide(DMF) as a solvent and tetraethylammoniumtetrafluoroborate(TEABF4), tetraethylammoniumhexafluorophosphate(TEABF6), tetrabutylammoniumtetrafluoroborate(TBABF4) and tetrabutylammonium hexafluorophosphate(TBAPF6) as an electrolytes(active material). The concentrations of electrolytes were in the range of 0.2~1.2 N, the volume ratios of PC and DMF as a mixed solvent system, were 90：10, 80：20, 70：30, 60：40, 50：50, and 40：60 vol%. Electrochemical characteristics such as electric conductivity, internal resistance, and electric capacitance of fabricated unit cells were measured after the moisture of activated material was removed with molecular sieve. Electrochemical characteristics were better in mixed solvents system than in mono solvent system. The mono solvent system of 1.0 N electrolyte of GBL/TEABF4 with activated carbon cloth electrodes showed better result but the mixed solvent system with PC and DMF/TEABF4(50：50 vol%) and the concentration of 1.0 N electrolyte showed the best characteristics. Internal resistance was 3.47 Ω and specific capacitance was 19.1 F/g respectively.y.

상변화형 광디스크는 직접 반복기록에 의한 고속기록, 고밀도화가 가능하고 높은 전송속도, 재생신호의 C/N (carrier to noise) 비가 좋은 장점을 가지고 있으나 반복되는 열에너지에 의한 디스크의 변형과 소거도의 저하, 기록 반복성의 저하가 문제가 된다. 이러한 반복성의 저하를 개선하기 위해 적절한 디스크의 구조와 기록막의 상하부에 유전체 보호막인 ZnS-SiO2 박막층을 삽입하였다. 박막 제조시 많은 실험변수의 제어를 위해 다꾸찌 방법을 통하여 타겟 R.F. Power 200W, 기판 R.F. Power 20W, 아르곤 압력 4mTorr, 전극거리 6cm의 최적조건을 얻을수 있었다. TEM과 XRD분석 결과, 전극거리가 가까워질수록 높은 증착속도로 인하여 미세한 조직구조를 가지고 있으며, 일정거리 이상 가까워지면 막의 morphology에 나쁜 영향을 끼침을 알 수 있었다. 이러한 막의 morphology의 영향으로 투과율이 감소하는 것을 확인할 수 있었다. AFM과 SEM분석에서는 전극거리가 가까워질수록 높은 증착속도로 인하여 morphology에 나쁜 영향을 끼치고 있음을 확인할 수 있었다. 최적조건에서 증착한 박막은 우수한 morphology를 가진 초미세구조의 치밀하고 결함이 없는 박막이었다. 이 박막은 상변화형 광디스크에서 열적 변형을 억제하고, 열전도를 감소시켜 우수한 유전체 보호피막의 역할을 할 수 있다. 그리고, 전극거리가 ZnS결정립의 크기와 증착속도, morphology에 미치는 영향에 대해 고찰하였다.

A water-soluble conducting polymer (CPP400 Paste) containing a derivative of polythiophene with several dopant was investigated as an anode material for organic electroluminescent devices. The device of ITO/CPP 400 Paste/TPD/Alq3/Li:Al was fabricated, where CPP 400 Paste films were prepared by spin coating and TPD and Alq3, films were prepared by vacuum evaporation. It was found that the turn-on voltage, current density, and luminance of the devices were dependent upon the thickness of CPP 400 Paste film in the Electroluminescent and current-voltage characteristics of the devices. This phenomena were explained by the energy level diagram of the device with the energy levels of the CPP400 Paste obtained by cyclic voltammetric method.

운반체(감응물질)로 제 4급 인산염을 사용하여 PVC를 지지체로 하여 과염소산이온의 농도 10-6 M까지 선형적인 이온선택성 전극을 제작하였다. 운반체의 화학적구조와 함량 가소제의 종류 및 막 두께에 따른 전극의 기울기 선형응답범위 및 한계측정농도 등 전극전위특성을 고려하여 최적의 과염소산 이온선택성 PVC막 전극을 제조한 다음 측정 가능한 pH 범위 선택계수 및 전극의 교류임피던스 특성을 비교 검토하였다 운반체로 tetraoctyl-phosphonium perchlorate(TOPP) tetraphenylphosphonium perchlorate(TPPP) 및 tetrabutylphosponium perchlorate (TBPP) 등의 제 4급 인산염의 과염소산 이온 치환체를 사용하였다 알킬기의 탄소고리 수가 증가할수록 전극특성은 TBPP, 선형응답범위 10-1×10-6 M 및 한계측정농도는 9.66×10-7 M 이었으며 시판되고 있는 Orion 전극특성보다 좋은 결과를 나타내었다 전극전위는 pH3~11범위에서 ph의 영향을 받지 않았으며 CIO4 에 대한 방해이온의 선택계수 서열은 SO24 < F < Br < I 이었다 임피던스 측정결과 TOPP의 경우 등가회로는 용액저항 이중층용량과 벌크저항의 병렬 및 Warburg 임피던스의 직렬이었다 이 경우 용액저항은 거의 나타나지 않았고 확산에 의한 Warburg 임피던스는 크게 나타났으며 Warburg 계수는 1.32×1074 Ω cdot cm2/s1/2이었다.

50/50 vol% LSM-YSZ의 복합공기극(LSM=La1-xSrxMnO3(0≤x≤0.5))이 콜로이드 증착법에 의해 준비으며 주사전자현미경과 임피던스 분석기에 의해 연구되어졌다. 재현성있는 임피던스 스펙트럼들이 LSM-YSZ/YSZ/LSM-YSZ로 구성된 향상된 셀을 사용함으로써 얻어졌다. 이러한 셀들의 임피던스 스펙트럼들은 작동온도에 강하게 영향을 받았으며, 가장 안정된 조건은 900˚C에서 도달되어졌다. 900˚C에서 공기//공기 셀에 대해 측정된 전형적인 임피던스 스펙트럼들은 2개의 불완전한 호(depressed arc)로 구성되었다. LSM전극에 대한 YSZ의 첨가는 LSM-YSZ 공기극의 저항 감소를 가져왔으며, 전해질 표면의 불순물의 영향을 제거하기 위한 연마는 공기극 저항을 더욱 감소시켰다. 또한 촉매층(Ni 혹은 Sr)을 가진 LSM-YSZ 전극은 촉매층이 없는 경우에 비해 공기극 저항의 감소를 가져왔다. LSM-YSZ 공기극 저항은 전극조성, 전해질의 형태, 인가 전류에 의해 영향을 받았다.