본 연구에서는 플라즈마 화학 증착법으로 기판에 따른 DLC 박막의 접착력 변화를 조사하였다. 박막의 분리가 발생하기 시작하는 경우의 두께를 임계두께로 정하여 스크래치 테스터로 측정된 임계하중과 더불어 박막의 잡착강도값으로 사용하였다. 다이아몬드상 탄소박막은 실리콘 기판에서 가장 우수한 접착력을 가지는 것으로 나타났으며, 크롬>티타늄>철>세라믹 기판의 순으로 접착력이 감소하였다. XPS, AES 분석을 사용하여 계면에서 결합구조와 결합형태 등을 관찰하여 접착력과의 관계를 조사하였다. 그 결과 다이아몬드상 탄소박막의 접착강도는 막/기판의 계면에서의 탄화물 형성에 영향을 받으며, 계면에서의 초기산화물층에 큰 영향을 받는것을 확인하였다.

To determine an operational condition of an adhesion-type oil skimmer, it is important to estimate the withdrawal rate for a given driving velocity of the skimmer and material properties of the oil. As a theoretical model for this problem the formation of an oil film on a vertically driven flat plate is investigated. The previous steady-state analysis made in the field of coating industry are reviewed. These studies have been made under the assumptions of small Reynolds and capillary number, which is adequate for coating process but not for oil skimming. An alternative analysis based on the linear stability theory is made. Comparisons with the experimental results reveal that the stability analysis gives a correct estimation of the withdrawal rate for high capillary number at which the previous theory losses its validity.

강유전체 재료의 하부전극으로 사용되고 있는 Pt/Ti 박막의 접착력에 대한 열처리 분위기의 영향을 연구하였다. 시편의 접착력은 90˚ 필 테스트 방법을 사용하여 정량적으로 측정하였다. 열처리 후 사용된 분이기에 관계없이 모두 접착력이 감소하였는데 특히 산소분위기에서 열처리 한 시편의 접착력이 매우 크게 감소하였다. AES depth profile과 단면 TEM을 이용하여 계면반응을 관찰한 결과 산소열처리시에는 Ti가 외부에서 확산해 온 산소와 반응하여 rutile TiO2상이 형성됨을 알 수 있었다. 그러므로 산소열처리 후에 일어나는 접착력의 급격한 감소 원인은 열처리시 취약한 TiO2상이 형성되며 이로 인해 Ti 접착층이 고갈되기 때문임을 알 수 있었다.

각종 전자부품에 이용되는 백금막의 밀착력과 응집화 현상에 대해 연구하였다. 온도저항계수(TCR)의 열화 없이 밀착력을 향상 시키기 위해서 AI, Si의 산화물을 adhesion promoting layer로 이용한 결과 매우 우수한 밀착력과 TCR을 보였다. 질소분위기 600-900˚C의 온도범위에서 행한 열처리를 통해 응집화현상을 관찰한 결과 응집화는 기판거칠기에 따라 다른 양상을 보였다. Si3N4등의 기판거칠기가 작은 adhesion promoting layer를 이용한 시편의 경우 고온인 900˚C에서 응집화 현상이 발생되었다. 표면거칠기가 큰 AI-Si 산화물을 adhesion promoting layer로 이용한 시편의 경우 비교적 저온인 600˚C에서 응집화 현상이 발생했으며 800˚C이상의 열처리의 경우 중앙응집체와 응집체고갈지역이 형성되는 현상을 나타내었다.

Subhalfmicron ULSI의 컨택홀을 메꾸는 기술로 각광받고있는 전면도포(blanket W)법에서 부착특성고양층(glue layer)인 TiN막에대한 CVD-W의 부착특성을 조사하였다. 부착강도는 텅스텐막의 두께가 증가함에 따라 TiN막내의 응력의 감소로 인해 부착특성이 향상되었다. TiN막표면을 스퍼터 에칭하는 진처리를 실시할 경우 막표면의 불순물 제거, 표면 거칠기 증가등의 효과로 부착특성이 개선되었다. 또한 TiN막표면에 Ar이온 주입에 의한 손상을 줄 경우에도 TiN막 표면이 활성화되어 부착특성이 향상되었다.

전면증착법에 의한 W공정에서 부착특성고양층으로 사용되는 TiN막에 대한 CVD W막의 부착특성을 인장법(pulling method)과 스크래치법(scratch method)을 사용하여 조사하고, 주사전자현미경과 반사도측정에 의한 표면거칠기측정, 응력측정 및 SIMS depth profiling 등에 의하여 그 원인을 분석하였다. 스퍼터링법으로 형성한 TiN막상에 바로 W막을 증착한 경우와 TiN막을 열처리한 후에 W막을 증착한 경우 간에 두 막간의 부착특성은 큰 차이를 보였다. 전자의 경우가 후자의 경우보다 부착특성이 더 우수한 것으로 나타났는데, 이것은 열처리하지 않은 TiN막이 열처리한 TiN막에 비해 표면이 더 거칠고, 응력수준이 더 낮으며, 열처리한 TiN막내에는 산소성분이 존재하는 반면, 열처리 하지 않은 TiN막내에는 산소성분이 거의 들어있지 않기 때문이다. 또한 TiN막 두께가 증가함에 따라 응력의 증가로 인하여 TiN막에 대한 W막의 부착강도가 저하되었다.

The purposes of this study is to evaluate the adhesion in flexure and adhesion in tension between old-plain cement mortar and new-polymer cement mortar that has been widely used as finishing and repairing materials of RC structures. From the test results, the adhesion in flexure and adhesion in tension of polymer-modified mortar to plain cement mortar are much higher than that of plain cement mortar, and are increased with increasing polymer-cement ratio. The maximum strengths show at polymer cement mortar using EVA dispersion, and those are about 1.69 and 2.10 times respectively, plain cement mortar.

The purpose of this experimental study is to develop the waterborne silicon acrylic surface finishing material of parking lots. Adhesion strength experiment was conducted in order to enhance performance of the finishing material by adopting modified polyamide resin. The results qualified the standard regarding bond strength which is prescribed in KS F 4937. They are confirmed that the strength tend to increase as the amount of polyamide increased and could be an optimum surface finishing material applicable for parking lot floor.

This paper presents a study on the adhesive strength testing of self-adhesive waterproofing/anti-corrosion sheet used for waterproofing of the large diameter steel pipe interior of water treatment facilities. After the sheet has been applied, similar physical and chemical immersion conditions are simulated in the testing to determine the effects of deterioration through adhesion strength testing.

The purpose of this experimental study is to carry out test for the surface finishing material of parking lot using Cross-linking agent(Zinc Oxide). The specimen was fabricated by KS F 4937, Cross-linking agent 2%, 3%, 4% is mixed in water soluble acrylic resin. As a result, bond strength of surface finishing material using Zinc oxide 4% was confirmed to be superior than surface finishing material using ordinary Acrylic resin.

In this paper, the slope adhesion force of the developed green slope soil was evaluated by simulating rainfall intensity. From the results, the slope failure didn't occur at all conditions. As the slope angle increases, however, the damage decreased. The developed green slope soil is considered to have sufficient adhesion capacity to the slope.

Reinforced concrete is used as a main construction because it is excellent durability and strength. However, the problem of durability decrease due to enlargement, high-rise of structures and the cracking due to external force nowadays. Therefore, there is studying on the Textile Reinforced Concrete(TRC), which reinforcing bar changing into Textile. Also, studying on adhesion performance between concrete and Textile. Preceding studies have examined the adhesion performance of single fibers with no specific variable. It can not reflect about grid type and embedding length. Accordingly, on this study examines the change of bond strength according to bond length. As a result, the bond strength increased as the embedding length of the Textile increased, but there was not influence that the bond strength according to the lateral length.

This study is the adhesion strength of the sprayed metal in accordance with a proportion ratio of the Zn-Al. Results showed the most excellent adhesion strength for metal spraying Al100 For the metal spraying Zn100, ZnAl85, ZnAl95 exhibited a similar level of adhesion strength results.

본 연구는 3,3'-diindolylmethane(DIM)이 인간전립선암 세포인 PC3 세포와 DU145 세포의 부착, 이동, 침윤에 미치 는 영향을 살펴보았다. DIM은 PC3와 DU145 세포의 부착을 농도 의존적으로 억제하였다. 24시간동안 DIM으로 PC3 세포를 전 처리한 후 부착실험을 한 결과 농도 의존적으로 억제하였다. 그러나 암세포가 부착 시 DIM의 암세포 부착 억제가 전처리에 의한 부착 억제보다 효과적이었다. DIM 은 인간 전립선암세포의 이동과 침윤도 억제하였으며 24시 간 동안 PC3 세포를 DIM으로 전처리를 했을 때도 침윤 억제효과를 나타내었다. 또한 DIM의 억제효과는 세포주에 따라 다소 다른 경향을 보여 PC3 세포에 대한 억제효과가 DU145 세포에 대한 억제효과보다 큰 것으로 관찰되었다. DIM은 150 μM 까지 세포 독성이 관찰되지 않은 것으로 보고되고 있으므로 본 연구결과 DIM은 세포 독성이 없는 수준에서 인간 전립선암 세포인 PC3와 DU145 세포의 부 착, 이동, 침윤을 효과적으로 억제하여 전립선암 전이 억제 제로 이용될 수 있을 것으로 사료된다.

The purpose of this study is to develop eco-friendly finishing materials of acrylic emulsion-modified mortars using lightweight aggregate carrier which contains pyroligneous liquid. Four types of light-weight aggregate carriers such as perlite, vermiculite, charcoal and zeolite are selected. The acrylic emulsion-modified mortars are prepared with light-weight carrier replacements to dolomite of 0, 5, 10, 15, 20%, and tested for flowability, adhesion in tension, water absorption coefficient and antibiosis. As a result, the flowability of acrylic emulsion-modified mortars using zeolite light-weight is improved with increasing light-weight carrier content. The adhesion in tension of acrylic emulsion-modified mortars using lightweight carrier is satisfied with KS requirement. Especially, the adhesion in tension of acrylic emulsion-modified mortars using light-weight aggregate carrier at a high temperature of 40oC are better than the low temperatures of 0oC and 20oC. The water absorption coefficient of acrylic emulsion-modified mortars using light-weight aggregate carriers is increased with increasing light-weight carrier content. However, the water absorption coefficient is satisfied with KS requirement. The antibiosis of acrylic emulsion-modified mortars using zeolite light-weight carrier is remarkably improved with increasing light-weight carrier content.

This paper describes the evaluate adhesion area effects on structural performance of structural sealants. In this experimental, glass panel thickness and initial construction depth of sealant are 12 and 5mm. Principle variable is addition of sealants : 5, 10, 15mm. Prior to add sealant, adhesion part carried out cover with primer. Test method is based on the bending test. Loading method is to put sand on the center of the glass panel in order to the wind load applied to the actual condition. Test results indicated that addition of sealants is not improve the peak load.