Furfurylidene acetophenone derivatives were synthesis, it was measured that nucleophilic addition made use of UV at a wide pH 1.0~13.0 range in 30% dioxane-H2O solution, 25℃. On the basis of general base catalysis, substitutent effect, confirmation of nucleophilic addition products, it was measured the reaction rate of furfurylidene acetophenone derivatives for the pH change. It may be concluded that a part was unrelated to pH and another part was in proportion to concentration of hydroxide ion: Above pH 10.0. sulfide anion adds to the double bond (Michael type addition), a part having no concern with pH, addition reaction to double bond is initiated by addition of neutral thiourea molecule. From the result of measurement the reaction rate, nucleophilic addition of furfurylidene acetophenone derivatives confirmed to the irreversible first order. Through measurement the substituent effect. It found that reaction rate was accelerated by electron attracting group. On the basis of these findings, nucleophilic addition of thiourea for the furfurylidene acetophenone derivative was proposed a fitting mechanisms.

BaTiO3물질은 뛰어난 유전체로 널리 알려져 왔으며 특히 Heywang등이 제안한 PTCR특성은 이 물질의 응용범위를 세라믹 필터, 회로보호소자, 온도감지소자 및 저항가열장치 등으로 확대시켰다. 이러한 특성의 발현기구는 아직까지 밝혀지지 않은 상태이지만 제 특성을 향상시키기 위한 노력은 계속되어왔다. 특히 개발목적에 맞게 온도에 따른 정저항 특성(PTCR; Positive temperature constnat of resistivity phenomena)을 설계하려는 시도가 계속되어 왔으며 그 중에서도 페로브스카아트계의 2가와 4가의 양이온 자리를 등가나 원자가가 다른 양이온으로 치환하여 특성을 개선하려는 시도가 계속되어 왔다. 특히 Ca2+나 Sr2+는 Ba2+자리를 치환할 수 있는 물질로 개별적인 첨가에 대한 연구는 많은 연구자들에 의해 진행된 상태이지만 최종적인 영향이나 해석에 대해서는 연구자들간에 이견이 많은 상태이다. 이번 실험에서는 BaTiO3계에 합성한 (Ca, Sr)TiO3를 Ca와 Sr의 상대적인 비를 변화시키면서 전체적인 첨가량을 변화시켜 그에 따른 전기적 특성 및 미세구조를 살펴보았다. (Ca, Sr)TiO3의 첨가로 상온저항 및 PTCR특성을 변화시킬 수 있었으며 이를 통해 PTCR물질의 활용범위를 넓힐 수 있는 발판을 마련할 계기가 되었다. 특히 기존의 연구가 주로 개별적인 Ca나 Sr의 첨가에 의한 미세구조와 전기적 특성변화의 연구에 치중해 있었던 것과는 달리 Sr과 Ca을 함께 치환하여 상대적인 비가 특성에 더 중요한 영향을 끼치는 것을 확인하였으며 적절한 합성비를 선택하면 퀴리온도에서의 저항변화폭을 유지하면서 상온저항을 낮출 수 있음을 확인하였다.

급냉응고법을 이용하여 고용한도 이상으로 Mn량을 첨가할 때 Mn량에 따른 인장특성의 변화와 시효특성을 조사하였다. 원심분무법으로 AI-4.7%Zn-2.5%Mg-0.2%Zr합금에 Mn량을 각기 달리 첨가한 급냉응고 분말을 제조 하였다. 이 분말을 냉간압축, 진공 탈가스처리를 한 후 15:1로 압출하여 봉상 시편을 만들었다. 분말의 미세조직은 α-AI수지상과 수지상간 편석부로 이루어져 있으며 Mn첨가에 따라 조직의 변화는 관찰되지 않았다. 빠른 냉각속도로 인하여 2.0%Mn을 첨가한 경우에도 초정 Mn상을 발견할 수 없었다. 압출재의 미세조직은 아결정립으로 이루어져 있으며 약간의 제2상들이 관찰되었다. 대부분의 Mn 분산상은 압출후 용체화처리 과정에서 형성되었으며 시효경화량은 Mn양에 관계없이 일정하였다. 460˚C에서 1시간 용체화처리하고 120˚C에서 24시간 시효처리한 경우 최대의 시효경도값을 나타내었다. 인장강도는 Mn첨가량에 따라 증가 하였는데 이것은 Mn분산상의 밀도증가에 의한 것으로 확인되었다. 2.0%Mn을 첨가한 합금의 시효후 인장강도는 590MPa, 연산율은 4%를 보였다.

CuO의 첨가가 BiNbO4 세라믹스의 마이크로파 유전특성과 소결거동에 미치는 영향에 대하여 연구하였다. CuO의 첨가량이 증가함에 따라 액상의 생성에 의해 소결성이 증가하여 시편의 밀도는 증가하며 유전상수는 소결온도가 증가함에 따라 증가하는 경향을 보였다. Qxfo값은 CuO 첨가량이 0.065wt%이고 소결온도가 940˚C일 때 최대값을 나타내며 그 이상 CuO 첨가량을 증가하였다. 소결온도 920˚C-960˚C, 소결시간 2시간일 때의 고주파 유전특성으로는 유전상수가 43.6, Qxfo값이 13,200 이상, τf =-14.36ppm/˚C을 얻었다.

In recent times the potential application of the high speed steel produced by HIP process for wear resistant and cutting materials are increasing. In this work the microstructure of Anval 30 produced by HIP process was investigated and the effect of WC, TiC addition on microstructure formation and wear properties were studied. After HIP process at 1150 , the original feature of spherical raw powders was not removed and consequently, nonuniform microstructure was formed. However the WC added by simple powder mixture incereased the sinterbility of high speed steel and uniform microstructure formed. The wear characteristics of Anval 30 with carbide addition were tested at RT and . The uniform microstructure played an more important role in wear resistance as compared with the hardness.

Spring sown oat crops were grown during early March to late June in 1993~1994. The crops were harvested at different stage of maturity to determine the yield performance, chemical components and net energy value of the plants for silage utilization. The p

The effects of added VC, CrC and TaC on the microstructures and properties of submicron WC-10%Co cemented carbides. The relative sintered density of compact was increased by addition of CrC but decreased oppositely by addition of VC or TaC. The growth of WC grains was significantly suppressed by addition of these carbides. The hardness of these alloys was increased by addition of other carbides and showed a maximum value by simultaneously added VC and CrC. The transverse rupture strength(T.R.S.) was in- creased by addition of CrC, while it was decreased by addition of VC or TaC. The relative sintered density and T.R.S. of these alloys were improved by HIP-treatment. The maximum T.R.S. was 328kg/mm in the Wc-10%Co cemented carbide with addition of 0.5%VC.

Fluorenylidene chalcone derivatives were synthesized by condensation. The structure of these compounds were ascertained by means of UV, melting point, IR and 1H-NMR spectra. The nucleophilic addition reaction kinetics of Thioglycolic acid to fluorenylidene chalcone was investigate by UV in 20% dioxane-H2O at 25℃. The rate equation which were applied over a wide pH1.0~13.0 range. On the basis of general base catalysis and confirmation of addition reaction product, the nucleophilic addtion reaction kinetics of thioglycolic acid to fluorenylidene chalcone were measured by the pH change. From the result of the above caption, a plausible nucleophilic addition reaction mechanism of thioglycolic acid to fluorenylidene chalcone was proposed. These compounds may be used as the starting materials for the preparation of the engineering plastics or the germicide.

원소 분말을 합성하여 Ti5SI3 화합물을 합성하는 방법을 연구하였다. 합성법으로서는 기본적으로 반응소결법을 사용하였으며, 치밀화를 위하여는 유사-열간 정수압 성형법(PHIP, pseude-hot isostatic pressing)을 사용하였다. 반응소결법에서는 분말의 입도, 반응온도 및 유지시간이 소결밀도에 영향을 주었으며, PHIP법에 의한 치밀화에서는 압력 및 유지 간이 주요 변수로 사용되었다. 이들 변수중 미세한 입도와 유지시간이 기공을 감소시켰다. 또한 Cu의 첨가 영향을 연구하였는데, 약 6wt%이내의 Cu 첨가는 밀도 향상에 좋은 영향을 미쳤다. 반응소결 및 PHIP를 통해 Ti5SI3 -Cu의 상대밀도를 약 99%까지 높일 수 있었으며, 이때 Cu의 효과는 감도지수 부합됨을 확인하였다.

The removal of residual captan in carrot and kale by storage temperatures and the addition of condiments was investigated. The quantities of residual captan after sticking and drying of captan in carrot and kale were 0.958 and 26.12 ppm, respectively. During storage of 20 days at 15, 3 and -17℃, the levels of the residual captan in carrot decreased to 0.008 (removal rate: 99.2%), 0.228(76.2%) and 0.380 ppm (60.3%), and those in kale decreased to 1.21 (95.4%), 7.72 (70.5%) and 15.06 ppm (42.3%), respectively. The higher removal rate of residual captan was observed at the higher storage temperatures. When the condiments of soy sauce, green onion, garlic and vinegar added to the carrot which contaminated with the captan and then stored at 15℃ for 24hrs, the residual levels of captan decreased to 0.207 (removal rate: 78.4%), 0.196 (79.5%), 0.164 (82.8%) and 0.209 ppm (78.2%), respectively, showing the garlic was the most effective. However, the residual levels in kale were 2.27 (91.3%), 12.70 (51.4%), 16.42 (37.1%) and 13.70 ppm (47.5%), respectively under the same condition, indicating the soy sauce was the most effective. The removal rates of residual captan in carrot and kale were significantly higher with the addition of the condiments than those of the controls that without the condiments.

제 3원소가 첨가된 금속간 화합물 TiAI 금속간 화합물 분말을 PREP법(플라즈마 회전전극법)으로 제조하여, 통.방전 강압소결법에 의해 치밀한 소결체를 만들었다. 이에 대해 첨가 원소의 종류와 열처리에 따른 고온 및 상온 압축 특성의 변화를 조사하였다. 소결체의 미세조직은 γ/α2 lamella로 이루어진 완전 변태구조였고, 결정립의 크기는 140-150μm였으며 계단형 결정립계를 나타내었다. 소결체를 (α+γ)구역인 1300˚C에서 2시간 동안 열처리한 결과, 모든 조성의 시편이 등축점 γ와 lamella로 이루어진 전형적인 duplexrn조로 변태하였다. 상온 압축 시험에서 시편은 파괴될 때까지 가공경화 현상이 나타났으며, Cr을 첨가한 시편이 가장 큰 파괴응력과 변형률을 나타내었다. 한편, 고온 압축 시험의 경우 온도상승 때문에 가공경화의 속도가 감소되었고, 800˚C에서는 가공경화와 회복이 균형을 이루는 소위 정상 상태의 변형을 보였다.

고주파 저손실 재질로 사용되고 있는 Mn-Zn 페라이트의 제조공정 중 소결조건과 Ta2O5첨가가 Mn-Zn 페라이트의전력손실에 미치는 영향에 대해서 연구하였다. 등조성선을 따라 냉각하기 위하여 컴퓨터를 사용해서 정확하게 산소분압을 조절하였으며 적절한 등조성선을 선택함으로써 보다 좋은 손실특성을 얻을 수 있었다. CaO-SiO2 첨가계에 Ta2O5를 0ppm에서 400ppm으로 변화시켜 가며 첨가하였으며, Ta2O5 가 400ppm 첨가되었을 경우 균일한 grain 성장과 더불어 낮은 전력손실을 나타내었다. 온도에 상응하는 상평형 산소분압을 정확히 맞춰 냉각할 경우 전력손실 최소값이 질소 분위기에서 냉각시킨 시편보다 높은 온도쪽으로 이동됨도 확인할 수 있었다.

저손실 망간징크 페라이트에서 CaO-SiO2첨가는 입계에 높은 전기저항층을 형성시켜 와류에 의한 손실을 감소시키는 것으로 알려져 있다. 본 실험에서는 Nb2O5 를 제 3의 첨가제로 사용하여 저손실 망간징크 페라이트에서의 전자기적 물성변화를 관찰하였다. Nb2O5 300ppm 이상 첨가시 부분적인 과대입자 성장이 관찰되었으며, 200ppm 첨가시 CaO-SiO2만 첨가한 시편에 비하여 밀도가 증가하였다. Nb2O5 첨가시에는 100ppm 이하의 SiO2첨가에서 우수한 전력손실 특성이 나타났으며, 고온 소결시 Nb2O5-CaO를 첨가한 시편에서 낮은 전력손실을 나타내었다.

기계적합금화한 Al-8wt.%(Ti+Zr)합금의 열적안정성에 미치는 Zr첨가의 영향에 대하여 조사하였다. Ti에 대한 Zr의 첨가비가 증가함에 따라 고온에서 장시간 노출에 따른 합금의 경도감소가 저하되어 합금의 열적안정성이 향상된 결과를 나타내었는데 이는 TEM 관찰결과 분산입자의 조대화가 억제되었기 때문이었다. XRD, SAD 및 EDS 분석결과 이러한 분산입자들은 DO2+와 DO23구조를 갖는 Al3(Ti+Zr)삼원계 금속간화합물이었으며 특히 DO23Al3(Ti+Zr)은 Zr의 첨가비가 증가함에 따라 보다 작은 Al기지와의 격자간불일치도를 갖는 방향으로 격자상수가 변화하여 합금의 열적안정성 향상에 주된 기여를 한 것으로 생각된다

This experiment was conducted to investigate the effects of wheat bran addition on the fermentative quality and dry matter digestibility(Dh4D) of rye silage. This hexbage was ensiled by the conventional methods in small glass silo of 0.82 liter with addit