PURPOSES : The aim of this study is to review freeze-and-thaw testing apparatuses, develop a freeze-and-thaw testing setup with a test protocol, test the freeze-and-thaw properties of soils collected from different parts of South Korea, and suggest an index for frost susceptibility criteria for soils found in South Korea. METHODS : Based on a literature review, a new freeze-thaw testing setup was developed. In addition, a test protocol was developed for freeze-thaw testing. Soils collected from different parts of South Korea and bedding sand used for block pavements were tested to determine whether the measurements from the newly developed test setup could capture important freeze-thaw characteristics of the soils. Finally, to develop local frost susceptibility criteria, a parameter including both the vertical deformation and thermal conductivity characteristics of the soils was suggested. RESULTS : The results from the laboratory experiments indicate that the newly developed freeze-and-thaw setup captures the required parameters to quantify the responses of soils subjected to cyclic freeze-and-thaw testing. In addition, a vertical deformation of up to 2.437 mm is measured. Moreover, seven soils out of the nine tested soils are classified as having a medium frost susceptibility, whereas the remaining two show low frost susceptibility. The bedding sand experiment also shows that there is a possibility of having a frost susceptible condition based on the moisture content. When submerged, the bedding sand is classified as having a medium frost susceptibility. CONCLUSIONS : The "HEART" freeze-thaw testing setup was able to capture the parameters required for evaluating the frost susceptibility of soils. This setup and testing procedure could be further used to test and prepare criteria for classifying the frost susceptibility of soils found in South Korea.

한본 연구에서는, 철근콘크리트 보 구조물의 동결융해에 따른 장기거동특성 및 최종 파괴형태를 비교 분석하고자 하였다. 철근콘크리트 보 시험체와 재료 시험체를 제작하여, 동결융해 챔버를 이용하여 동결과 융해를 반복적으로 수행하였다. 동결융해를 위하여 기존의 시험법을 참고하여 철근콘크리트 구조물에 대한 시험을 수행 하였다. 동결융해에 따른 콘크리트의 재 료특성 변화와 철근콘크리트 보 구조물의 거동특성 변화를 통하여 동결융해에 대한 영향을 평가하였다. 제안된 동결융해 시험법을 통하여 콘크리트 공시체의 압축강도가 약 19%감소하였다. 철근콘크리트 보 시험체의 경우, 콘크리트의 표면 강도가 동결 융해에 의하여 감소되어 사인장 균열이 발생하여, 재료적 강도 감소에 의한 구조물의 성능이 감소함을 확인하였다. 또한, 사인장 균열이 발생한 동결융해 시험체의 에너지 소산능력이 동결융해를 거치지 않은 시험체와 비교하여 적게 발생하였다.

The aim of this study was to evaluate the effects of orvus es paste(OEP) on the sperm characteristics during freezing in boar semen. Semen quality was evaluated the motility, membrane integrity, mitochondria function, acrosome status, viability and abnormality. Boar semen were frozen until 5℃ for 2 hours using cell freezer and making the straws, and then freezing by lowing the straws into styrofoam box on the 8cm above the LN2 and plunged into LN2 for cryopreservation. In different concentration of OEP (0, 0.25, 0.5 and 1.0%) into cryo-extender, sperm motility, membrane integrity, acrosome status, viability and mitochondria function were significantly higher in 0.5% OEP than those of any other groups, but sperm abnormality were highest in 1.0% OEP group among all treatment groups (P<0.05). In the relationships of the evaluation methods for sperm viability, CBB vs membrane integrity, CBB vs HO/PI and CBB vs mitocondria function were positively correlated (0.67~0.92). Among the evaluation methods, CBB vs membrane integrity, CBB vs HO/PI and CBB vs mitocondria function were significantly correlated (P<0.001). These results of this study indicate that supplementation of 0.5% OEP in boar semen cryo-extender can improve the semen quality.

The purpose of this study is to evaluate the tensile strength of GFRP and BFRP Rebar after exposure to environmental factors of deterioration (alkali, freezing -thawing) in order to present that as basic data for the application of FRP Rebar as concrete reinforcement. As a result, in the exposure of an alkali environment, the deterioration of fiber-resin was accelerated as the temperature increased, and it was found that there was an insignificant effect on freezing-thawing.

As the industrialization is rapidly growing, the quantities of industrial waste glass have been quickly increased. However the most of them are not recycled. Therefore, it is needed to investigate the possibility of industrial waste glass as concrete material ingredient. In this paper, it is compared and evaluated that the characteristics of freeze-thaw resistance according to industrial waste glass substitution ratio in concrete specimens. From the results, the weight change was not affected by the waste glass substitution ratio. And, the relative dynamic modulus of elasticity was increased slightly with the waste glass substitution ratio. The relative dynamic modulus of elasticity was above 80% up to 300cycles in all of the mixes.

아스팔트 콘크리트 포장 파손 중 40cm-50cm 지름과 5cm-10cm 깊이를 갖는 움푹 파이는 형태의 포장 파손을 포트홀(pothole)이라고 한다. 포트홀 파손 발생 메커니즘은 아스팔트 혼합물에 수분이 침투하고, 아스팔트 바인더와 골재의 점착력이 침투한 수분에 의하여 약화되어 발생한다. 따라서 아스팔트 콘크리트 포장의 포트홀은 주로 장마 기간에 많이 발생하지만 최근 들어 지구 온난화의 영향으로 겨울철 강우 또는 강설의 증가와 제설제의 영향으로 겨울과 봄에도 많이 발생하고 있다. 본 연구에서는 아스팔트 콘크리트 포장에 발생한 포트홀 파손을 효율적으로 상온에서 보수할 수 있는 보수 재료에 대하여 25℃에서 간접인장강도시험을 수행하고, 5회 동결융해 반복 후 간접인장강도시험을 수행하여 인장강도비(TSR, Tensile Strength Ratio)를 산정하였다. 이때 사용된 우레탄 개질 아스팔트 포트홀 보수재는 목표 공극률 4%대의 혼합물을 사용하였으며, 비교대상 상온 보수재는 사전 혼합된 형태로 사용되고 있는 기성 제품 2종류를 선정하였다. 각각의 포트홀 보수재는 양면 50회 다짐을 수행하여 공시체를 제작하였다. 동결융해 조건은 KS F 2398에 따라서 영하 18℃에서 16시간 방치한 후 60℃ 항온수조에서 24시간 담그는 것을 동결융해 1회로 보고 5회 반복한 후 간접인장강도시험을 수행하였다. 5회 동결융해 반복시험 후 인장강도비가 우레탄 개질 아스팔트 포트홀 보수재의 경우 35%이며, 비교 대상 상온 포트홀 보수재는 각각 67%와 66%로 나타났다. 우레탄 개질 아스팔트 보수재의 인장강도비가 다른 두 혼합물보다 50%정도 인장강도비가 작은 것으로 나타났지만 5회 동결융해 반복 시험 후 25℃의 인장강도값의 경우 비교 대상인 상온포트홀 보수재가 개발중인 상온 포트홀 보수재보다 각각 36%와 12%로 매우 작은 것으로 나타났다.

Domestic portland cement(OPC) is made up of clinker, gypsum and 5% of admixtures. If 5% of Admixture contents of portland cement add to 10%, CO2 reduction effect can be expected. In this study, Freezing and Thawing test of concrete using limestone powder was evaluated.

This study evluated the Freeze-thaw and scaling resistance characteristic of high early-strength low heat cement concrete. The result Freeze-thaw and scaling resistance appeared to be excellent, and using high early-strength low heat cement can be applied to concrete structures of road facilities.

원형 구조물의 보수/보강 및 FRP를 구조부재로 활용한 신설 구조물 시공을 위해서는 일정한 곡률반경을 갖는 곡면 FRP 부재가 요구된다. 그러나 현재까지 FRP 곡면부재는 수작업 (hand-lay-up) 또는 필라멘트 와인딩 (filament winding) 작업에 의해서만 생산이 가능하였으며, 대량 연속생산에는 한계가 있다. 또한 일반적으로 인발성형법 (pultrusion method)으로 생산된 FRP 부재가 상대적으로 물리적 특성이 우수한 것으로 알려져 있다. 따라서 FRP 부재를 일정곡률을 유지하며 인발로 뽑아낼 수 있는 신개념의 곡면 FRP 부재 인발성형법 제안 및 성형장비를 개발, 곡면 FRP 제품을 생산하였으며, 본 연구에서는 곡면 FRP 부재를 이용한 구조물 보수/보강시 야기될 수 있는 FRP와 콘크리트 부착면의 동결융해 영향을 분석하였다.

콘크리트 구조물은 일반적으로 동결융해 작용을 받는 조건에 노출되고, 이러한 동결융해작용은 콘크리트의 공극구조를 변화시키고, 콘크리트의 내구성을 저하시킬 우려가 있다. 따라서 본 연구에서는 동결융해작용에 의한 콘크리트 내부공극구조 변화와 동결융해작용을 받은 콘크리트의 내구특성을 평가하고자 하였다. 실험결과, 기존의 동결융해 평가기법에 따르면 모든 배합에서 우수한 내구성능을 나타내었으나, 동결융해 작용에 노출됨에 따라 50~100nm 크기의 공극이 크게 증가하며, 콘크리트 염화물침투저항성이 저하하였다. 수중양생 콘크리트의 공극구조와 염화물 침투저항성은 선형관계를 보이지만, 동결융해작용을 받으면 내부공극구조의 변화로 선형관계가 저하하였다. 동결융해작용과 염화물침투를 동시에 받는 구조물의 내구성 평가기준에 대한 재검토가 필요할 것으로 판단된다.

일반적으로 철근콘크리트 건축물은 외부의 기후에 노출되어 있어 겨울에서 이른 봄까지 동결과 융해의 반복적인 작용에 영향을 받는다. 이러한 동결융해 작용은 콘크리트의 균열을 발생시키거나 콘크리트 표면의 박리를 일으켜 내구성 저하의 원인이 된다. 본 연구에서는 철근콘크리트 보의 동결융해 노출에 따른 휨 거동특성의 평가를 위해 주근비와 동결융해 사이클을 변수로 하였다. -18~4℃의 온도범위에서 150 및 300 사이클의 동결융해에 노출시킨 실험체를 비롯하여 14개의 축소모형 실험체를 제작, 단조 및 반복하중 하에서 실험을 실시하였다. 실험결과를 통해 동결융해에 노출되어있는 철근콘크리트 보의 휨 거동특성을 평가하는데 기초적인 자료를 제시하고자 하였다

해양콘크리트의 대표적인 내구성 열화요인이라 할 수 있는 동결융해나 염해의 경우는 콘크리트내의 공극특성에 따라 침투 및 확산특성이 크게 상이하게 되는데, 이는 동결융해저항성 확보를 목적으로 사용되고 있는 AE제의 종류나 사용량 그리고 그의 경시변화 특성 등과 매우 밀접한 관계가 있다. 따라서 본 연구에서는 굳지않은 콘크리트의 목표 공기량을 각각 4～6%와 8～10%로 계획하여 실내시험을 실시한 후, 모의부재에서는 4～6%를 대상으로 평가하였다. 실험결과, 경화콘크리트의 공기량은 재령 7일에서 각각 2.5～5.2%, 재령 28일에서는 각각 2.4～5.1%정도로서 비빔직후 목표공기량의 절반수준인 것으로 나타났고, 동결융해 반복에 따른 스케일량은 목표공기량 8～10%의 경우가 4～6%에 비해 미미한 수준에서 다소 유리한 것으로 평가되었다. 한편, 모의부재에서 채취한 코어공시체의 동결융해 및 염화물 확산특성에서는 동일배합조건의 실내시험 결과에 비해 다소 불리한 것으로 나타났는데, 실내실험 결과에 비해 동결융해는 106%, 염화물 확산계수는 160% 수준인 것으로 나타났다.