We used a conventional activated sludge process to treat a paper wastewater, and then the effluent was treated with an ozone oxidation process as advanced process to remove non-degradable materials. It was found that the removal efficiency rates of the organic matter has been rapidly increased initially, and then it was almost constant after this period. The concentration of ozone should be recommended to maintain approximately 8.3 mg/L during this operation to keep the CODmn value below 100 mg/L and ozone contact time longer than 60 min.

Oxidation characteristics of benzene as a VOC were investigated using a fixed bed reactor system over transition metal catalysts. The transition metal catalysts were made by using transition metal nitrate reagent and various support materials such as γ-Al2O3, and TiO2. The parametric tests were conducted at the reaction temperature range of 200～500℃, benzene concentration of 2,000～3,000 ppm with space velocity of 10000 hr-1. The property analyses such as BET, SEM, TGA and the conversions of catalytic oxidation of VOC were examined. The experimental results showed that the BET surface areas of catalyst are 86.4∼167.7m2/g, the pore volumes are 0.049∼0.056cm3/g, and the average pore sizes of catalyst are 27∼44Å, which mean the meso pore. It was also found that the conversion of benzene oxidation reaction at 400∼500℃ with Cu/γ-Al2O3+TiO2 catalyst showed 90∼100%, which indicate that the transition metal catalyst with composite supports is very effective for the oxidation of benzene.

Thermal emissivity of nuclear graphite was measured with its oxidation degree. Commercial nuclear graphites (IG-110, PECA, IG-430, and NBG-18) have been used as samples. Concave on graphites surface increased as its oxidation degree increased, and R value (Id/Ig) of the graphites decreased as the oxidation degree increased. The thermal emissivity increased depending on the decrease of the R (Id/Ig) value through Raman spectroscopy analysis. It was determined that the thermal emissivity was influenced by the crystallinity of the nuclear graphite.

In this study, toluene catalytic oxidation was investigated using various metal components (Cu, Ce, Ni, La and Zr) supported on Used FCC zeolite for the application of the waste recycling and odor reduction. Among the metals, 5 wt% Cu/zeolite showed the best catalytic activity. 100 % conversion was achieved at 300℃ which was 50℃ lower than that of other metal components. As increasing the amount of doped Cu, the CuO was formed and the surface area and pore size were decreased. By the reduction treatment before toluene oxidation, the catalytic activity of the oxidation below 250℃ was improved. No decrease of conversion was observed during the continuos reaction at 300℃ for 48 h.

Thermal emissivity of commercial nuclear graphites (IG-110, PCEA, IG-430 and NBG-18) following changes in oxidation degrees were examined. Specimens were oxidized to 0%, 5%, and 10% in air flow of 5l/min at 600℃ using a furnace, and the thermal emissivities were measured using an infrared spectrum analyzer. The measuring temperatures for the thermal emissivity were 100℃, 200℃, 300℃, 400℃ 500℃. Also density and porosity of the specimens were observed to compare with thermal emissivity. Results showed that emissivity increased with oxidation, and the 10% oxidized NBG-18 showed the highest emissivity (0.890) which value is larger for 24% than the value of as-received specimen. Investigation of factors affecting the emissivity revealed that increases in the surface roughness and porosity due to oxidation were responsible for the increase in emissivity after oxidation.

Fe-Cr steels are the most promising candidate for interconnect in solid oxide fuel cells. In this study, an effective, dense and well adherent (LaSr)(CrCo) [LSCC] coating layer was produced onto 430 stainless steel (STS-430) by atmospheric plasma spraying and the oxidation behavior as well as electrical properties of the LSCC coated STS-430 were investigated. A significant oxidation of pristine STS-430 occurred at in air environment, leading to the formation of and scale layer up to after 1200h, and consequently increased an area specific resistance of . Although the plasma sprayed LSCC coating contained the characteristic pore network, the coated samples presented apparent advantages in reducing oxidation growth of STS-430, resulting a decrease in oxide scale thickness of at after 1200h. The area specific resistance of the LSCC coated STS-430 was much reduced to after exposure at for 1200h, compared to that of the pristine STS-403.

Silicon dioxide as gate dielectrics was grown at 400˚C on a polycrystalline Si substrate by inductively coupled plasma oxidation using a mixture of O2 and N2O to improve the performance of polycrystalline Si thin film transistors. In conventional high-temperature N2O annealing, nitrogen can be supplied to the Si/SiO2 interface because a NO molecule can diffuse through the oxide. However, it was found that nitrogen cannot be supplied to the Si/SiO2 interface by plasma oxidation as the N2O molecule is broken in the plasma and because a dense Si-N bond is formed at the SiO2 surface, preventing further diffusion of nitrogen into the oxide. Nitrogen was added to the Si/SiO2 interface by the plasma oxidation of mixtures of O2/N2O gas, leading to an enhancement of the field effect mobility of polycrystalline Si TFTs due to the reduction in the number of trap densities at the interface and at the Si grain boundaries due to nitrogen passivation.

Graphite for the nuclear reactor is used to the moderator, reflector and supporter in which fuel rod inside of nuclear reactor. Recently, there are many researches has been performed on the various characteristics of nuclear graphite, however most of them are restricted to the structural and the mechanical properties. Therefore we focused on the thermal property of nuclear graphite. This study investigated the thermal emissivity following the oxidation degree of nuclear graphite with IG-11 used as a sample. IG-11 was oxidized to 6% and 11% in air at 5 l/min at 600˚C. The porosity and thermal emissivity of the sample were measured using a mercury porosimeter and by an IR method, respectively. The thermal emissivity of an oxidized sample was measured at 100˚C, 200˚C, 300˚C, 400˚C and 500˚C. The porosity of the oxidized samples was found to increase as the oxidation degree increased. The thermal emissivity increased as the oxidation degree increased, and the thermal emissivity decreased as the measured temperature increased. It was confirmed that the thermal emissivity of oxidized IG-11 is correlated with the porosity of the sample.

High modulus pitch based carbon fibers (HM) were exposed to isothermal oxidation using tube furnace in carbon dioxide gas to study the oxidation kinetics under the temperature of 800-1100℃. The kinetic equation f=1--(-atb) was introduced and the constant b was obtained in the range of 1.02~1.42. The oxidation kinetics were evaluated by the reaction-controlling regime (RCR) depending upon the apparent activation energies with the conversion increasing from 0.2 to 0.8. The activation energies decrease from 24.7 to 21.0 kcal/mole with the conversion increasing from 0.2 to 0.8, respectively. According to the RCR, the reaction was limited by more diffusion controlling regime for the HM fibers with the conversion increasing. Therefore, it seems that the oxidation which is under the diffusion controlling regime takes place continuously from the skin to the core of the fiber.

The investigation is to modify the mechanical and chemical properties of Mg alloys using a combination of rapid solidification and surface treatment. As the first approach, was gas atomized and pressure sintered by spark plasma sintering process (SPS), showing much finer microstructure and higher strength than the alloys as cast. Further modification was performed by treating the surface of PM Mg specimen using Plasma electrolytic oxidation (PEO) process. During the PEO processing, MgO layer was initiated to form on the surface of Mg powder compacts, and the thickness and the density of MgO layer were varied with the reaction time. The thickening rate became low with the reaction time due to the limited diffusion rate of Mg ions. The surface morphology, corrosion behavior and wear resistance were also discussed

1,4-Dioxane is an EPA priority pollutant often found in contaminated ground waters and industrial effluents. Conventional water treatment techniques are limited to decompose this compound effectively. Therefore, an advanced oxidation process system (AOP) was used for the degradation of 1,4-dioxane. This research investigates the effect of adding oxidants, such as ozone, air, and H2O2 during the UV irradiation of 1,4-dioxane solution. In order to analyze 1,4-dioxane, a modified 8270 method, which is an improved method of U.S EPA 8720, was used. Degradation efficiencies of 1,4-dioxane by only UV irradiation at various temperatures were not significant. However, The addition of oxidants and air bubbling in the UV irradiation system for 1,4-dioxane decomposition showed the higher 1,4-dioxane degradation rate. And, during AOP treatment the tendency of TOC changes was similar to that of 1,4-dioxane decomposition rate.

This study was conducted to investgate the effect of gamma irradiation on the lipid oxidation, olfactory properties, fatty acid isomer and volatile compound profiles of five different oil sources. Three plant oils, canola oil, corn oil and soy oil, and two animal fat, tallow and fish oil, were irradiated with 0, 5, 10, and 20 kGy level of dose by Co-60 as a radiation source. Lipid oxidation parameters, FFA, POV and TBARS, were determined according to the AACC and AOCS method. Olfactory property of irradiated oil sources was analyzed using electronic nose (FOX3000, AlphaMOS Co., France) with 12 metal oxide sensors and the result was interpreted using principle component analysis program. Fatty acid isomer profiles and volatile compound profiles of irradiated oils were also measured by GC and GC-MS, respectively. Although the free fatty acid level of oil were the highest by high dose level (20 kGy) of irradiation, changes of both TBARS and POV values by gamma irradiation were varied between oil sources and irradiation level of dose. Electronic nose analysis showed a distinct difference among dose levels of irradiation. Although there was no new volatile compound produced by gamma irradiation, amounts of each volatile compounds were increased by irradiation. Only cis isomer, 9c12c15c of linolenic acid was dose-dependently decreased as irradiation level increased but there was no difference among other isomer profiles of linoleic acid and linolenic acid by gamma irradiation. This study showed that changes in physico-chemical properties of both plant and animal oil were remarkable by gamma irradiation. Therefore, a further study should be needed to scrutinize the interaction among lipid oxidation, production of volatile compounds and off-flavor, and isomerization of fatty acid by gamma-irradiation.

This study was carried out to investigate the effects of addition of aged garlic extract (AGE) on the color and lipid oxidation of ground chicken during refrigerated storage. The leg meat from 6 weeks-broiler was chopped and added with 4% of distilled water (control) and AGE, respectively, and then stored at 4±0.2℃ for 8 days. The commercial garlic was aged for the relatively short time (40-90℃/300 hr →natural dryness/40 hr→20-30℃/30-50 hr). The pH value was not significantly different between control and AGE-added chicken. The TBARS level of chicken was remarkably inhibited by addition of AGE during storage. In CIE color values, AGE-added chicken showed lower L* and higher b*, C* and Ho values than those of control during storage. Therefore, the addition of AGE in ground chicken enhanced the lipid oxidative stability and change to dark color.

The microstructure, mechanical and electrochemical properties of plasma electrolytic coatings (PEO) coatings on Mg-4.3 wt%Zn-1.0 wt%Y and Mg-1.0 wt%Zn-2.0 wt%Y alloys prepared by gas atomization, followed by compaction at 320 for 10 min under the pressure of 700 MPa and sintering at 380 and 420 respectively for 24 h, were investigated, which was compared with the cast Mg-1.0 wt%Zn alloy. All coatings consisting of MgO and oxides showed porous and coarse surface features with some volcano top-like pores distributed disorderly and cracks between pores. In particular, the surface of coatings on Mg-1.0 wt%Zn-2.0 wt%Y alloy showed smaller area of pores and cracks compared to the Mg-4.3 wt%Zn-1.0 wt%Y and Mg-1.0 wt%Zn alloys. The cross section micro-hardness of coatings on the gas atomized Mg-Zn-Y alloys was higher than that on the cast Mg-1.0 wt%Zn alloy. Additionally, the coated Mg-1.0 wt%Zn-2.0 wt%Y alloy exhibited the best corrosion resistance in 3.5%NaCl solution. It could be concluded that the addition of Y has a beneficial effect on the formation of protective and hard coatings on Mg alloys by plasma electrolytic oxidation treatment.

The oxidation of nanocrystalline powder has been conducted to investigate its influence on the electromagnetic wave absorption characteristics of the soft magnetic material. Oxidation occurred primarily on the surface of nanocrystals. Oxidation reduced the real part of complex permeability due to the reduction of the relative volume of the powder, which otherwise contributes to the permeability. Oxidation reduced the absorption efficiency of the sheet at frequencies over 1GHz, indicating that the relative contribution of skin depth increments to the absorption was not significant. The pulverization and milling process lowered the optimum crystallization temperature of the material by because of the internal energy accumulated during the fragmentation and powder thinning processes.

Oxidation behavior and microstructural characteristics of nano-sized Sn powder were studied. DTA-TG analysis showed that the Sn powder exhibited an endothermic peak at and exothermic peak at with an increase in weight. Based on the phase diagram consideration of Sn-O system and XRD analysis, it was interpreted that the first peak was for the melting of Sn powder and the second peak resulted from the formation of phase. Microstructural observation revealed that the powder, heated to under air atmosphere, consisted of agglomerates with large particle size due to the melting of Sn powder during heat treatment. Finally, fine SnO2 powders with an average size of 50nm can be fabricated by controlled heat treatment and ultrasonic milling process

질산, 불산 및 과염소산을 사용하여 플루토늄 옥사이드 을 녹여 Pu 기준용액을 제조한후 UV-Visible-Near IR 분광기를 이용하여 Pu 흡수 스펙트럼 특성을 관찰하였다. 산성, 중성 및 알칼리 매질에서 Pu(III), Pu(IV) 및 Pu(VI)에 대한 분광학적 특성을 조사하였다. 또한 알칼리 및 산 농도 증가에 따른 Pu(VI) 흡수 스펙트럼에 대한 특성 피크 세기 및 위치를 관찰하였다. 염산 및 수산화나트륨 매질에서 환원제 첨가에 따른 Pu(VI) 산화수 변화를 측정하였다.