[ BaO·Nd2O3·5TiO2 ] (BNT) ceramics modified with a borate glass containing Ba, Nd and Ti as glass constituents were investigated with regard to their sintering behavior and microwave dielectric properties. An addition of iso-component glass significantly improved the sinterabilty of the BNT ceramics and lowered the sintering temperature. A maximum density of 5.29 g/cm3 and an x-y shrinkage of 17% were obtained for BNT ceramics containing 10wt.% of the glass sintered at 1100˚C. The dielectric composition without the glass additive was only slightly densified at 1100˚C. The resulting sample exhibited two crystalline phases, BaNd2Ti5O14 and Ba2Ti9O20, regardless of sintering temperature and glass content. When >10wt.% glass was added, exaggerated grain growth with a less uniform microstructure was found, resulting in the subsequent reduction of the fired density and the dielectric properties. BNT ceramics containing 10wt.% of the isocomponent glass sintered at 1100˚C for 4 h showed promising dielectric properties of k = 71.3 and Q = 1,330.

Hydroxyapatite (HAp) and biphasic calcium phosphate (BCP) nano powders were synthesized using the microwave-assisted synthesis process dependent on pH and microwave irradiation time. The average size of a powder was less than 100 nm in diameter. Through in-vitro cytotoxicity tests by an extract dilution method, the HAp and BCP nano powders have shown to be cytocompatible for L-929 fibroblast cells, osteoblastlike MG-63 cells and osteoclast-like Raw 264.7 cells. The activation of osteoblast was estimated by alkaline phosphatase (ALP) activity. When the HAp and BCP were treated to MG-63 cells, alkaline phosphatase activities increased on day 3, compared with those of the untreated cells. Also, the collagen fibers increased when the HAp and BCP powders suspension were treated to MG-63 cells, compared to those of the untreated cells. Quantitative alizarin red S mineralization assays showed a trend toward increasing mineralization in osteoblast cultured with powder suspension. In conclusion, hydroxyapatite and biphasic calcium phosphate appeared to be a bone graft substitute material with optimal biocompatibility and could be further applied to clinical use as an artificial bone graft substitute.

The purpose of this research was to study treatment characteristics of main odor substances, such as Trimethylamine and Acetaldehyde, by using 600 Wand 200 W microwave plasmas. Ar and air were used as plasma gases and a cylindrical SiC/Zeolite filter having several Ø 2~3 ㎜ size holes was used as a trigger to obtain a stable plasma even with a relatively low microwave power. The 600 W Ar plasma was used to destroy relatively high concentrated TMA and acetaldehyde from 500 ppm to 2200 ppm and their DREs (Destroy and Removal Ratios) were measured. The 200 W air plasma was also used to measure DREs for TMA and acetaldehyde Jowly concentrated in 4.5 odor strength. The results demonstrated that the Ar plasma produced 70% to 90% efficiency in removing odors substances. The 200 W Air plasma, which was operated at the relatively lower energy level, produced 90% or even above higher efficiency for the odorous materials. It was expected that the air plasma was effectively used to control odorous materials emitted from relatively a small size plant process.

Thin films of carbon-nano materials (CNMs) of different morphology have been successfully deposited on ceramic substrate by CVD at temperatures 800℃, 850℃ and 900℃ using plant based oils in the presence of transition metal catalysts (Ni, Co and Ni/Co alloys). Based on the return and insertion loss, microwave absorption properties of thin film of nanocarbon material are measured using passive micro-Strip line components. The result indicates that amongst CNMs synthesized from oil of natural precursors (mustered oil - Brassica napus, Karanja oil - Pongamia glabra, Cotton oil - Gossipium hirsuta and Neem oil - Azadirachta indica) carbon nano fibers obtained from neem's seed oil showed better microwave absorption (~20dB) in the range of 8.0 GHz to 17.90 GHz.

High temperature dielectric constants of the various ceramic materials have been measured using cavity perturbation method. The measurements were applied to refractory, traditional and fine ceramic powder compacts from room temperature to . Calibration constant in the equation suggested by Hutcheon et al., was determined from the dielectric constants of reference specimen (teflon and alumina) at room temperature. From these results, informations on the refectory materials were obtained for the microwave kiln design and understanding of the microwave heating effects of ceramics have been improved.

Using microwave synthesized HAp nano powder and polymethyl methacrylate (PMMA) as a pore-forming agent, the porous biphasic calcium phosphate (BCP) ceramics were fabricated depending on the sintering temperature. The synthesized HAp powders was about 70-90 nm in diameter. In the porous sintered bodies, the pores having were homogeneously dispersed in the BCP matrix. Some amounts of pores interconnected due the necking of PMMA powders which will increase the osteoconductivity and ingrowth of bone-tissues while using as a bone substrate. As the sintering temperature increased, the relative density increased and showed the maximum value of 79.6%. From the SBF experiment, the maximum resorption of ion was observed in the sample sintered at .

We present a systematic study of the heating and pre-sintering behavior of porous copper powder metal compacts. We employ a TE102 single mode microwave system to position the samples in the separated electric field (E) or magnetic field (H) anti-node of the cavity. We observe significant differences in the heating, pre-sintering, and microstructure evolution of the samples due to the individual fields. We note that sample history (whether heated first in the E-field or H-field) greatly effects a difference in heating trends and subsequent heating behavior and does not appear to be solely a thermal process.

In a companion paper, we have presented so-called Spatio-Spectral Maximum Entropy Method (SSMEM) particularly designed for Fourier-Transform imaging over a wide spectral range. The SSMEM allows simultaneous acquisition of both spectral and spatial information and we consider it most suitable for imaging spectroscopy of solar microwave emission. In this paper, we run the SSMEM for a realistic model of solar microwave radiation and a model array resembling the Owens Valley Solar Array in order to identify and resolve possible issues in the application of the SSMEM to solar microwave imaging spectroscopy. We mainly concern ourselves with issues as to how the frequency dependent noise in the data and frequency-dependent variations of source size and background flux will affect the result of imaging spectroscopy under the SSMEM. We also test the capability of the SSMEM against other conventional techniques, CLEAN and MEM.

원자력 발전소에서 발생하는 고체 방사성 폐기물인 이온교환수지, 제올라이트, 활성탄 및 슬러지 에 포함된 성분 원소 분석을 위한 산분해 조건을 확립하였다. 방사성 폐기물의 분해 에는 흔합산을 이용한 밀폐형 극초단파 산분해법을 사용하였으며, 제안한 방법에 따른 산분해 후의 용액은 맑고 색이 없는 투명한 상태임을 확인할 수 있었다. 또한, 산분해 과정을 거친 각각의 용액 시료는 ICP-AES와 AAS를 사용하여 분석하였고, 모의 방사성 폐기물에 첨가한 5종의 금속 원소들은 이상의 높은 회수율을 보여주었다. 화학적 특성을 고려하여 제안된 산분해 조건에 의해 용액화된 중저준위 방사성 폐기물의 성분 원소 분석은 최적의 유리화 기술 개발을 위한 기초 자료로 유용하게 사용될 수 있을 것으로 판단된다.

WC-6wt%Co hard metal powders were sintered by a 2.45 GHz multimode microwave applicator in Ar atmosphere. Microwave sintering of WC-6wt%Co powder lowered the sintering temperature and shortened the processing time in less than two hours than by a conventional method. Microstructures of the sintered specimen were studied with scanning electron microscope (SEM) and no abnormal grain growth was observed. Mechanical properties were similar to the values of the specimens sintered by a conventional method. Specimen sintered at 135 for 30 minutes ,hewed 99%, 20.5 GPa and 8.1 MPa of theoretical density, hardness and fracture strength, respectively.

Solar flares present a number of radiative characteristics indicative of kinetic processes of high energy particles. Proper understanding of the kinetic processes, however, relies on how well we can separate the acceleration from transport characteristics. In this paper, we discuss microwave and hard X-ray bursts as a powerful tool in investigating the acceleration and transport of high energy electrons. After a brief review of the studies devoted to the kinetic process of solar flare particles, we cast them into a simple formulation which allows us to handle the injection, trap, and precipitation of flare electrons self-consistently. The formulation is then taken as a basis for interpreting and analyzing a set of impulsive and gradual bursts occurred on 2001 April 6 observed with the Owens Valley Solar Array, and HXT/WBS onboard Yohkoh satellite. We quantify the acceleration, trap, and precipitation processes during each burst in terms of relevant time scales, and also determine ambient density and magnetic field. Our result suggests that it should be the acceleration property, in particular, electron pitch angle distribution, rather than the trap condition, that is mainly responsible for the distinctive properties of the impulsive and gradual flares.