The error function can be calculated based on the Simpson method through a subroutine program. An integration program by FORTRAN language was made for diffusion equations of extended source with infinite extent and limited extent. The results on some alloying elements such as C, Co, Cr, Mn, Mo, Ni and V's diffusion in iron, showed the diffusion distance for Ni and Mo can only be and more distance for Co at common sintering temperature of . To refine the particle size of the added elements down to a scale of micrometers is an effective way to get homogeneous distribution.

New PM route via bulk mechanical alloying is developed to fabricate the solid solution semi-conductive materials with and for 0 < x, y < 1 and to investigate their thermoelectric materials. Since is n-type and both and are p-type, pn-transition takes place at the specified range of germanium content, x, and tin content, y. Through optimization of chemical composition, solid-solution type thermoelectric semi-conductive materials are designed both for n-and p-type materials.

급속소결방법인 고주파유도가열 소결법과 펄스전류활성 소결법을 이용하여 습식 볼밀링으로 혼합한 WC-8wt.%Ni분말에 60MPa의 압력과 고주파유도가열장치의 경우 전체 용량 (15kw)의 90%에 해당하는 고주파출력을, 펄스전류활성 소결장치의 경우 2800A의 펄스전류를 가하여 치밀한 소결체를 2분이내의 짧은 시간에 제조하였다. WC 초기입자크기가 증가함에 따라 제조된 소결체의 입자크기와 평균자유행로는 증가하였다. 또한 WC 결정립 크기가 증가함에 따라

새로운 급속소결방법인 고주파유도가열 소결법과 펄스전류활성 소결법을 이용하여 습식 볼밀링으로 혼합한 WC-8wt.%Co분말에 60MPa의 압력과 90%의 고주파출력 또는 2800A의 필스전류를 가하여 상대밀도가 98.6% 이상인 초경재료를 2분이내의 짧은 시간에 제조하였다. 초기의 WC분말의 입도가 미세해짐에 따라 고주파유도가열 소결법과 펄스전류활성 소결법 모두 소결시간이 단축되는 경향을 보였으며 그 소결체의 결정립 크기도 감소하였다. 고주파유도가열 소결

From a viewpoint of heat stress at high temperatures and contact thermal resistance, it is confirmed that the optimal structure is the skeleton structure using Cu substrate on the cooling side, which has excellent heat conductivity and the optimal installation method is to adopt a carbon sheet and a mica sheet to the high temperature side, where Si grease is applied to the low temperature side, under pressurized condition. The power of the developed modules indicated 0.5W in an module and 3.8 W with a SiGe module at 823K, respectively.

This paper presents the influence of the compositions of sintered Ti-Ni alloys on their thermo-mechanical properties. The Ti-Ni alloys having various compositions from 50at%Ni to 51at%Ni were sintered using elemental Ti and Ni powders by a pulse-current pressure sintering equipment. The deformation resistance in stress-strain curves increased with an increase in Ni content. In the case of Ti-50at%Ni, tensile strength and elongation were more than 500 MPa and 7%, respectively. The increase in Ni content also makes the transformation temperatures lower. The deformation resistance at a test temperature change from 293K and 353K in isothermal tensile test increased with elevating test temperature.

Processing of W-Cu graded materials from attritor-milled W-CuO mixtures is described. The powder reduction steps are investigated by TG and XRD analyses and by microstructural observations (SEM, TEM). Sintering of reduced powder with different compositions is analysed by dilatometry. Sintering behaviour of the graded component processed by co-compaction of a 10/20/30wt%Cu multi-layer material is briefly discussed. Liquid Cu migration is observed and smooths the composition gradient. Perspectives to control this migration are discussed.

A theoretical model is applied to the analysis of thermomechanical properties of FGMs in this study. Functionally graded composites ( FGMs) consisted with 10 layers gradually changing volume fractions of Al and were fabricated using the pressureless infiltration technique. FGMs plates of total thickness of 3mm, 5mm and 7mm with fairly uniform distribution and compositional gradient of reinforcement in the Al matrix throughout the thickness was successfully fabricated. The curvature of FGM plates was measured to check the internal stress distribution predicted via a theoretical model for the analysis of thermo-mechanical deformation. The evolution of curvature and also internal stresses in response to temperature variations could be predicted for the different combinations of geometric thickness of FGM plates. Theoretical prediction of thermally induced stress distribution makes it possible to design FGM structures without any critical failure during the usage of them.

Ceramic-Metal Functionally Graded Materials (FGM) are of great interest for application as Thermal Barrier Coating (TBC) or Wear Resistant Coating (WRC). Spark Plasma Sintering (SPS) is a promising techniques for time-saving consolidation of laminated/graduated powder systems: SPS is a pressure-assisted electrical sintering method which directly applies a pulsed DC current as heat source. In the present work, production of FGMs by means of Spark Plasma Sintering is considered; effect of sintering condition on density, hardness and fracture toughness is studied. Problems correlated to this new processing technology are discussed.

Austenitic stainless steel has been used as a corrosion resistance material. However, austenitic stainless steel has poor wear resistance property due to its low hardness. In this investigation, we apply powder composite process to obtain hard layer of Stainless steel. The composite material was fabricated from planetary ball milled SUS316L stainless steel powder and WC powder and then sintered by Pulsed Current Sintering (PCS) method. We also added TiC powder as a hard particle in WC layer. Evaluations of wear properties were performed by pin-on-disk wear testing machine, and a remarkable improvement in wear resistance property was obtained.

Metallic foams have a combination of attractive properties such as high specific mechanical properties and good energy absorption characteristics. This paper presents the properties of steel foam sandwiches produced using powder metallurgy approach. Metallic powder, solid polymeric binder and a foaming agent are dry-mixed and molded into the desired shape. The molded powder mix is then heat-treated to foam, debind and sinter the material. The resulting material has an open cell structure with high porosity. The structure and properties of sandwiches specimens produced with the process are presented and discussed.

A novel production method for porous metal components has been developed by applying powder space holder (PSH) method to metal powder injection molding (MIM) process. The PSH-MIM method has an industrial competitive advantage that is capable of net-shape manufacturing the micro-sized porous metal products with complicated shapes and controlled porosity and pore size. In this study, the small impeller with homogeneous micro-porous structure was manufactured by the PSH-MIM method. The effects of combinations in size and fraction of PMMA particle on dimensional tolerance and variation of sintered porous specimens were investigated. It was concluded that the PSH-MIM method could manufacture commercially microporous metal components with high dimensional accuracy.

Stainless steel sludge is generated as a waste in the grinding process, and the possibility of recycling stainless steel is considered here. In this study, we considered the possibility of using the stainless steel sludge as metal powder for MIM or raw material for metal foam. For the MIM process, the metal powder will need some improvement, and flotation and spheroidizing processes of the sludge are necessary. For fabrication of the metal foam, untreated sludge can be used, and steel foam about 90% porosity is produced.