To realize high-performance thin film solar cells, we prepared CIGS by the co-evaporation technique on both sodalime and Corning glass substrates. The structural and efficient properties were investigated by varying the thickness of the Mo:Na layer, where the total thickness of the back contact was fixed at 1μm. As a result, when the Mo:Na thickness was 300 nm on soda-lime glass, the measured Na content was 0.28 %, the surface morphology was a plate-like compact structure, and the crystallinity by XRD showed a strong peak of (112) preferential orientation together with relatively intense (220) and (204) peaks as the secondary phases influenced crystal formation. In addition, the substrates on soda-lime glass effected the lowest surface roughness of 2.76 nm and the highest carrier density and short circuit current. Through the optimization of the Mo:Na layer, a solar conversion efficiency of 11.34% was achieved. When using the Corning glass, a rather low conversion efficiency of 9.59% was obtained. To determine the effects of the concentration of sodium and in order to develop a highefficiency solar cells, a very small amount of sodium was added to the soda lime glass substrate.

본 연구에서는 H12MDI(4,4'-methylene dicyclohexyl diisocyanate)를 이용한 수분산 폴리우레탄 수지를 합성한 다음 방염제로 활용이 되고 있는 2-인산암모늄(ammonium dihydrogen phosphate) 수용액을 수분산 우레탄 수지에 적하량을 점차 증가시켜 변화하는 물성을 피혁(leather)에 표면 코팅처리된 상태 및 열풍 건조시킨 필름의 물성을 측정 분석하였다. 내용제성 측정 결과 높은 내용제성 물성을 지닌 폴리우레탄 수지에 2-인산암모늄의 함량에 따른 물성적 변화는 크게 없었으며 모두 높은 물성치를 나타내었다. 인장 강도 측정치에서는 폴리우레탄 단독 필름의 측정치가 3.114 kgf/㎟로 가장 높은 수치를 나타내었으며, 2-인산암모늄의 합량이 제일 높은 DPU-AD3가 가장 낮은 인장력 2.510 kgf/㎟을 나타내었다. 또한 내마모도 측정에서는 DPU가 제일 높은 50.50 ㎎.loss로 우수한 물성변화를 나타내었고, 연실율의 경우역시 우레탄 단독 코팅인 DPU가 602 %로 가장 높은 수치를 나타내었다. DSC측정결과 2-인산암모늄의 함유가 높은 DPU-AD3이 Tm 값이 384℃로 고온에서 가장 안정한 수치를 나타내었다.

목 적: 안구건조증의 일반적인 치료제로 사용되는 포비돈과 히알루론산염이 포함된 인공누액이 하이드로 젤 콘택트렌즈에 미치는 영향을 다양한 조건에서 분석 하였다. 방 법: 본 연구에 사용된 친수성 하이드로젤 콘택트렌즈의 제조를 위해 교차결합제인 EGDMA(ethylene glycol dimethacrylate)와 HEMA(2-hydroxyethyl methacrylate)를 기본 조합으로 사용하여 참조물을 제조하였다. 또한 20%의 NVP(n-vinyl-2-pyrrolidone)와 MMA (methyl methacrylate)를 첨가하여 함수율 별로 다양하게 중합하였다. 공중합된 콘택트렌즈를 인공누액에 각각 1시간, 2시간 그리고 72시간 침지시킨후 제조된 렌즈의 함수율과 접촉각을 측정하였다. 결 과: 제조된 콘택트렌즈의 기본 물성을 측정한 결과, 포비돈 참조물의 경우, 함수율 27.22~48.13%, 접촉각 70.48~41.43°의 범위로, 히알루론산염 참조물의 경우, 함수율 26.42~48.42%, 접촉각 70.21~44.66°의 범위로 나타났다. 또한 제조된 콘택트렌즈를 인공누액에 침지시킨 후 측정한 물리적 특성은 포비돈을 포함한 인공누액의 경우, 함수율 26.10~47.90%, 접촉각 43.54~81.23°의 범위로, 히알루론산염을 포함한 인공누액의 경우, 함수율 24.89~48.35%, 접촉각 38.56~68.58°의 범위로 나타났다. 침지 시간에 따른 물성 변화는 포비돈의 경우 함수율의 감소 및 접촉각의 증가, 히알루론산염의 경우 함수율 및 접촉각의 감소를 나타내었다. 결 론: 포비돈과 히알루론산염을 포함한 인공누액은 친수성 하이드로젤 콘택트렌즈의 함수율과 접촉각에 영향을 주는 것으로 나타났다.

Yacon (Smallanthussonchifolius) is a root crop that contains high amounts of fructo-oligosaccharides (FOS). FOS has a sweet taste, is low in calories, and is known to promote intestinal tract health. In this study, various yacon concentrates were substituted for sugar in white pan bread to obtain healthy benefits from the use of FOS. The quality characteristic changes during storage of the white pan breadswith 0, 25, 50, 75 and 100% of added yacon concentrates instead of sugar were investigated. During storage, the water contents and water activities of the breads made with high amounts of yacon concentrates changed less than in those made with only sugar. The hardness and chewiness of the breads made with high amounts of yacon concentrates had lower values than those made with only sugar. Thus, bread made with yacon concentrates might exhibit increased moisture retention and decreased aging velocity. The substitution of yacon concentrates for sugar in pan bread improved the bread quality.

Recently, ultrafine grained (ufg, typically 100 > d > 500 nm) Ti-Fe eutectic materials have been highlighted due to their extraordinarily high strength and good abrasion resistance compared to conventional coarse grained (cg, d > 1μm) materials. However, these materials exhibit limited plastic strain and toughness during room temperature deformation due to highly localized shear strain. Several approaches have been extensively studied to overcome such drawbacks, such as the addition of minor elements (Sn, Nb, Co, etc.). In this paper, we have investigated the influence of the addition of Gd and Y contents (0.3-1.0 at.%) into the binary Ti-Fe eutectic alloy. Gd and Y are chosen due to their immiscibility with Ti. Microstructural investigation reveals that the Gd phase forms in the eutectic matrix and the Gd phase size increases with increasing Gd content. The improvement of the mechanical properties is possibly correlated to the precipitation hardening. On the other hand, in the case of Ti-Fe-Y alloys, with increasing Y contents, primary phases form and lamellar spacing increases compared to the case of the eutectic alloy. Investigation of the mechanical properties reveals that the plasticity of the Ti-Fe-Y alloys is gradually improved, without a reduction of strength. These results suggest that the enhancement of the mechanical properties is closely related to the formation of the primary phase.

This study was carried out to investigate the influence of glycerine on the properties of paper. Two types of glycerine treatment were used. First type, when making handsheets, glycerine was added in the plup slurry. Second type, copying paper was soaked in glycerine solution. Microwave treatment was used for the test of paper degradation. The obtained results were summarized as follows: 1. The glycerin was very effective to improve the property of softness. 2. The glycerine was helpful to increase sizing performance of paper as a fixing agent of sizing emulsion. 3. Curl tester was comparatively useful for the measuring of sizing degree.

Room temperature cure type of acryl-urethane coatings with high solid content were prepared in this study. Acrylic resins with 80% solid content were cured with hexamethylene diisocyanate (Desmodure N-3600). The cure time of prepared coatings BEHCC-84 (BEHC-84 : Tg=0℃) and BEHCC-87 (BEHC-87 : Tg=30℃), measured by rigid-body pendulum method, was recorded 8.3 hours and 3.8 hours, respectively. Dynamic viscoelastic experiment also revealed the glass transition temperature of BEHCC-84 and BEHCC-87 to be Tg=40.3℃ and Tg=43.3℃, respectively. It was found that the adhesion and flexural properties among various propeties of coatings were enhanced by the incorporation of caprolactone acrylate monomer into the acrylic resins.

김치를 10℃에서 8일간 숙성시켜 산도 0.6~0.7%로 숙성된 김치를 -70℃와 -20℃로 냉동하여 -20℃에서 저장하면서 배추 조직의 elasticity, hardness, 세포 조직의 변화, 드립양을 실험한 결과는 다음과 같다. -70℃에서 급속 동결한 것과 -20℃에서 완만동결한 냉동 김치중 배추조직의 elasticity는 냉동저장 15일까지 감소하다 일정하게 유지되었고 hardness는 거의 변화가 없었으며 냉동 방법에 따른 변화도 거의 나타나지 않았다. 투과 전자현미경으로 관찰한 결과 control의 경우 세포벽이 매우 두꺼우며 세포의 모양들이 잘 보존되어 있는 것을 볼 수 있었고 -20℃로 냉동 처리하여 해동시킨 세포벽들은 많이 손상되어 있음을 볼 수 있었으며 -70℃로 급속 냉동 시료의 경우 세포벽의 손상 정도가 -20℃로 냉동 처리한 시료보다 덜 파괴되어 있음을 볼 수 있었다. 한편 냉동 저장기간 동안 드립의 손실량의 변화는 -70℃로 냉동 처리한 시료의 드립양은 3~4%정도로 -20℃로 냉동 처리한 시료의 5~6%에 비해 적은 것을 알 수 있었다.

최근 고감성 PET 사를 이용하여 생산한 PET 직물은 고감성 의류용 직물로서 많이 사용되고 있다. 이러한 고감성 의류용 PET 직물은 다양한 공정을 거치면서 장력이나 열 등의 영향을 받음으로서 사의 물성의 변화를 초래하여 감성 의류용도의 PET 직물에 많은 결점을 유발시킴으로서 직물 생산시 공정조건 설정 등의 어려움에 직면하고 있다. 이러한 고감성 의류에 치명적인 문제를 유발하는 문제점에 관한 감성사 제조시의 공정조건 변화와 관련된 연구논문은 많이 발표가 되지 못하고 있다. 따라서 본 연구에서는 국내 7개 원사 Maker의 cake내의 Denier 별 PET 사의 물성을 균일한 길이의 Layer를 설정하여 분석, 조사하고 Layer 별 물성 차이와 습·건열 열처리 온도에 따른 사의 수축률 등을 비교함으로서 감성 의류용 직물 생산에 필요한 기초 물성 Data를 제공하고 PET 사의 품질향상을 도모함으로서 최종 감성 의류용 직물 소재 개발에 기여할 수 있는 기초자료를 제공하고자 한다.

0.9Pb(Mg1/3Nb2/3)O3-0.1PbTiO3계 완화형 강유전체에서 MnO2 첨가가 압전물성에 미치는 영향을 강유전성이 우세한 온도영역인 -40~30˚C의 온도범위에 걸쳐 조사하였다. MnO2 첨가에 의한 효과를 유전특성, 압전특성, 전계유기 변형특성 등의 영역에서 고찰하였다 MnO2 첨가량이 증가할수록 유전성 및 압전성은 hard piezoelectric의 경향을 나타내었다. 이러한 실험적 고찰로부터 첨가된 Mn은 강유전 도메인 분역을 고정하는 역할을 하는 것으로 제안되었다.