Optical imaging and spectroscopy of G353.2+0.9, the brightest part of the giant H II region NGC 6357, shows that this H II region is optically thin, contains "300 M⊙ of ionized gas and is probably expanding into the surrounding medium. Its chemical composition is similar to that found in other H II regions at similar galactocentric distances if temperature fluctuations are significant. The inner regions are probably made of thin shells and filaments, whereas extended slabs of material, maybe shells seen edge-on, are found in the periphery. The radio continuum and Hα emission maps are very similar, indicating that most of the optical nebula is not embedded in the denser regions traced by molecular gas and the presence of IR sources. About 1050 UV photons per second are required to produce the Hβ flux from the 1l.3'x10' region surrounding the Pis 24 cluster that is south of G353.2+0.9. Most of the energy powering this region is produced by the 03-7 stars in Pis 24. Most of the 2MASS sources in the field with large infrared excesses are within G353.2+0.9, indicating that the most recent star forming process occured within it. The formation of Pis 24 preceded and caused the formation of this new generation of stars and may be responsible for the present-day morphology of the entire NGC 6357 region.

High-solid coatings were prepared by blending of previosly synthesized acrylic resins and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, cross-hatch adhesion, 60˚specular gloss, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. As a result of Rigid-body pendulum visco-elasticity measurement, dynamic Tg values of cured films increased with dynamic Tg values.

본 논문은 상온상태의 폐아스팔트 포장재료를 가열재활용하여 기층용뿐만 아니라 표층용으로 활용함에 있어 재생 아스팔트 바인더의 특성을 연구한 것이다. 4종류의 RAP을 가지고 RAP 자체의 기본 물성을 시험하였다. 배합설계는 표층에는 RAP을 10, 20%를 첨가하였고, 기층에는 10. 20, 30%를 첨가하였다. 재생혼합물의 신규바인더로는 AC 60-80을 선정하였다. 침입도, 점도, GPC, TFO. 저온균열 저항성을 평가하기 위한 BBR 실험을 수행하였다. 절대점도와 GPC에서의 대형입도분자(LMS)를 지수함수 회귀분석을 통해 R2이 0.95 이상이었고 이것은 절대점도 추정에 GPC 결과가 상당히 정확함을 시사해주고 있다. RAP을 첨가한 재생 아스팔트 바인더의 PG 저온 등급은 일반 신규 바인더에 비해 한 단계 높은 등급을 나타내므로 저온균열에 대한 저항성은 약간 약한 것으로 나타났다.

Multi-walled carbon nanotubes (CNTs) were prepared by thermal chemical vapor deposition (CVD) and microwave plasma chemical vapor deposition (MPCVD) using various combination of binary catalysts with four transition metals such as Fe, Co, Cu, and Ni. In the preparation of CNTs from acetylene precursor by thermal CVD, the CNTs with very high yield of 43.6 % was produced over Fe-Co/Al2O3. The highest yield of CNTs was obtained with the catalyst reduced for 3 hr and the yield was decreased with increasing reduction time to 5 hr, due to the formation of FeAl2O4 metal-aluminate. On the other hand, the CNTs prepared by acethylene plasma CVD had more straight, smaller diameter, and larger aspect ratio(L/D) than those prepared by thermal CVD, although their yield had lower value of 27.7%. The degree of graphitization of CNTs measured by Id/Ig value and thermal degradation temperature were 1.04 and 602℃, respectively.

PU flame-retardant coatings (APHD) containing phosphorous were prepared by blending of hexamethylene diisocyanate-trimer, white pigment, dispersing agent, flowing agent, and previously prepared benzoic acid modified polyester (APTB) that contains phosphorous. Physical properties of the prepared APHD were examined. With the introduction of BZA (contained in APTB), the film viscosity and film hardness of APHD decreased. With the introduction of caprolactone group, the flexibility, impact resistance, accelerated weathering resistance of APTBs increased. Flame retardancy of the coatings was tested. In a vertical burning method, APHD shows 210~313 seconds, and in a 45˚ Meckel burner method, shows 1.3~4.0cm2 of char length, which indicates that the coatings are good flame-retardant coatings. Moreover, the amount of afterglow and flame retardancy of the coatings are decreased with increasing BZA content.

We present results of a H13CN J=1-0 mapping survey of molecular clouds toward the Galactic Center (GC) region of -1.6° ≤ l ≤ 2° and -0.23° ≤ b ≤ 0.30° with 2' grid resolution. The H13CN emissions show similar distribution and velocity structures to those of the H12CN emissions, but are found to better trace the feature saturated with H12CN (1-0). The bright components among multi-components of H12CN line profiles usually appear in the H13CN line while most of the dynamically forbidden, weak H12CN components are seldom detected in the H13CN line. We also present results of other complementary observations in 12CO (J=1-0) and 13CO (J=1-0) lines to estimate physical quantities of the GC clouds, such as fractional abundance of HCN isotopes and mass of the GC cloud complexes. We confirm that the GC has very rich chemistry. The overall fractional abundance of H12CN and H13CN relative to H2 in the GC region is found to be significantly higher than those of any other regions, such as star forming region and dark cloud. Especially cloud complexes nearer to the GC tend to have various higher abundance of HCN. Total mass of the HCN molecular clouds within |l|≤ 6° is estimated to be ~2 ×10 7 M⊙ using the abundances of HCN isotopes, which is fairly consistent with previous other estimates. Masses of four main complexes in the GC range from a few 10 5 to ~ 10 7 M⊙ All the HCN spectra with multi-components for the four main cloud complexes were investigated to compare the line widths of the complexes. The largest mode (45 km s-1) of the FWHM distributions among the complexes is in the Clump 2. The value of the mode tends to be smaller at the farther complexes from the GC.

This study was conducted to investigate the effect of physical properties and antioxidant activities of the beer made by Lycii fructus for development of functional beer. Physical properties such as Brix˚, pH and hunter values were determined and compared with commercial beer. L(lightness) value was not significant difference among beer, although a(redness) and b(yellowness) values were higher in Lycii fructus beer than those of the commercial beer. Total phenolic acid contents were 0.790 mg/mL in Lycii fructus beer and 0.603 mg/mL in commercial beer. Electron donatin ability was 93% in Lycii fructus beer and 87% in commercial beer. Lycii fructus beer showed higher SOD-liked activities than in the commercial beer. The relative antioxidant effects of the Lycii fructus beer showed 19% inhibitory effect on the peroxidation of egg yolk lecithin.

The high-solid coatings were prepared by blending the synthesized acrylic resin in the previous paper and hexamethylene diisocyanate-trimer and curing it at room temperature. The characterization of the films of the prepared coatings was performed. The impact resistance, 60℃ specular gloss, cross-hatch adhension, and heat resistance of the films proved to be good, and the pencil hardness and drying time proved to be slightly poor. Especially, there was a remarkable improvement in the heat resistance. This improvement may stem from the regular arrangement of ethyl groups introduced into the acrylic resin. From a viscoelastic measurement using a rigid-body pendulum, curing was accelerated with the Tg value. With the increase in Tg, log damp value was lowered and dynamic viscoelasic Tg of a cured film was increased.

김치를 10℃에서 8일간 숙성시켜 산도 0.6~0.7%로 숙성된 김치를 -70℃와 -20℃로 냉동하여 -20℃에서 저장하면서 배추 조직의 elasticity, hardness, 세포 조직의 변화, 드립양을 실험한 결과는 다음과 같다. -70℃에서 급속 동결한 것과 -20℃에서 완만동결한 냉동 김치중 배추조직의 elasticity는 냉동저장 15일까지 감소하다 일정하게 유지되었고 hardness는 거의 변화가 없었으며 냉동 방법에 따른 변화도 거의 나타나지 않았다. 투과 전자현미경으로 관찰한 결과 control의 경우 세포벽이 매우 두꺼우며 세포의 모양들이 잘 보존되어 있는 것을 볼 수 있었고 -20℃로 냉동 처리하여 해동시킨 세포벽들은 많이 손상되어 있음을 볼 수 있었으며 -70℃로 급속 냉동 시료의 경우 세포벽의 손상 정도가 -20℃로 냉동 처리한 시료보다 덜 파괴되어 있음을 볼 수 있었다. 한편 냉동 저장기간 동안 드립의 손실량의 변화는 -70℃로 냉동 처리한 시료의 드립양은 3~4%정도로 -20℃로 냉동 처리한 시료의 5~6%에 비해 적은 것을 알 수 있었다.

The core-shell latex particles were prepared by sequential emulsion polymerization of alkyl methacrylate and styrene(ST) by using an water-soluble initiator(APS) after preparing monomer pre-emulsion in the presence of an anionic surfactant(SDBS). In organic/organic core-shell polymerization, the pre-emulsion method, which minimized required quantity of sulfactant, has been used to increase the conversion rate and the stability of core-shell latex particles as well as to reduce the formation of secondary particle that cause problems of soap-free emulsion during shell polymerization. We used several methods to observe the core-shell structure. The core-shell structure was studied by measuring pH change during hydrolysis by NaOH, glass transition temperature(Tg) by differential scanning calorimeter(DSC), morphology of latex by transmission electron microscope(TEM) and change of particle size and distribution by a particle analyzer.

아스팔트는 노화에 따라 물리적 특성변화가 일어난다. 하지만 같은 수준으로 노화시킨 아스팔트 혼합물들임에도 골재와 결합재 등에 따라 서로 다른 강성이나 취성을 보인다. 이는 노화에 의한 바인더 특성 변화의 차이에 기인한 것인데 이와 같이 혼합물 내에서 바인더의 물리적 특성 변화 차이에 영향을 주는 요인에 대한 연구는 별로 없다. 따라서 본 연구에서는 아스팔트 혼합물의 노화 후추출한 바인더의 물리적 특성을 측정하고 물성 차이에 영향을 미치는 요인을 분석하였다. 폴리머 3종류와 골재 두 종류, 두 가지 입도, 두 종류의 아스팔트를 사용하여 32종류의 혼합물을 제조하고, 이를 장 단기 노화 처리하였다. 각 혼합물의 노화 후 Abson recovery 방법으로 바인더를 추출 회생하고 바인더 물성 시험(침입도, 동점도, 절대점도)을 수행하였다. 이를 SAS를 이용하여 통계 분석하였다. 바인더 시험에서 골재 종류와 폴리머가 노화시 물성변화에 차이를 가져오는 심각한 요인임을 알 수 있었고, 입도는 점도 변화에 큰 영향을 미치는 인자인 것임을 확인할 수 있었다. 본 연구 결과, 혼합물 내의 바인더 물성은 골재 종류, 입도, 개질제의 종류, 바인더의 종류 등의 다양한 요인에 의해 많은 영향을 받는 다는 것을 알 수 있었다.

Environmental friendly acrylic/urea high-solid paint(MUHC) were prepared through the curing reaction of acrylics resin(EBHC) containing 70wt% of solids content and butylated urea curing agent. The synthesis of EBHC Was done at 150℃ for 6 hours, and the results were obtained as follows : Mn=1830~2190, Mw 3290~4000, Mw/Mn=1.80~1.83 viscosity=110~352 cps, and conversion=82~92%. After the film was coated with MUHC, the various physical properties were measured. They showed that enhancement of the coating properties such as adhesion, flexibility, abrasion resistance, impact resistance, and water resistance could be expected through introdl1cing caprolactone acrylate component in acrylics resin for the high-solids content acrylics/urea coatings.

This study was carried out in order to produce useful material for the forest multiple use and forest protection by soil physico-chemical analysis of studied area in Mt. Palgong. The results of soil physico-chemical analysis and statistical analysis represented as following 2 points. 1. Soil depth was in the range of average 61.1 cm and soil texture was loamy sand and sandy loam except Donghwasa area. The part of solid phase and gaseous phase were higher than other areas, but liquid phase was less in verse. Soil water content was in an average 49.5%, penetrability was average and the average of soil hardness was . This data showed that soil water content, penetrability and soil hardness were good at Mt. Palgong forest soils. 2. Soil pH was the range of 3.4 to 6.0, organic carbon content was 2.8% that is nearly mean of the Korea brown forest soils, total N content is somewhat smaller than that of other places, and total average C/N ratios was 13.9. Average available concentration was 5.05 mg/kg that is lower than that of any others. The concentration of available P of coniferous forests is higher than that of deciduous forests. Exchangeable cations content is similar to those of the Korea brown forest soil and the order of the cation content extent is > > > .

아스팔트는 노화에 따라 물리적 특성변화가 일어난다. 하지만 같은 수준으로 노화시킨 아스팔트 혼합물들임에도 골재와 결합재 등에 따라 서로 다른 강성이나 취성을 보인다. 이는 노화에 의한 바인더 특성 변화의 차이에 기인한 것인데 이와 같이 혼합물 내에서 바인더의 물리적 특성 변화 차이에 영향을 주는 요인에 대한 연구는 별로 없다. 따라서 본 연구에서는 아스팔트 혼합물의 노화 후추출한 바인더의 물리적 특성을 측정하고 물성 차이에 영향을 미치는 요인을 분석하였다. 폴리머 3종류와 골재 두 종류, 두 가지 입도, 두 종류의 아스팔트를 사용하여 32종류의 혼합물을 제조하고, 이를 장 단기 노화 처리하였다. 각 혼합물의 노화 후 Abson recovery 방법으로 바인더를 추출 회생하고 바인더 물성 시험(침입도, 동점도, 절대점도)을 수행하였다. 이를 SAS를 이용하여 통계 분석하였다. 바인더 시험에서 골재 종류와 폴리머가 노화시 물성변화에 차이를 가져오는 심각한 요인임을 알 수 있었고, 입도는 점도 변화에 큰 영향을 미치는 인자인 것임을 확인할 수 있었다. 본 연구 결과, 혼합물 내의 바인더 물성은 골재 종류, 입도, 개질제의 종류, 바인더의 종류 등의 다양한 요인에 의해 많은 영향을 받는 다는 것을 알 수 있었다.

최근 고감성 PET 사를 이용하여 생산한 PET 직물은 고감성 의류용 직물로서 많이 사용되고 있다. 이러한 고감성 의류용 PET 직물은 다양한 공정을 거치면서 장력이나 열 등의 영향을 받음으로서 사의 물성의 변화를 초래하여 감성 의류용도의 PET 직물에 많은 결점을 유발시킴으로서 직물 생산시 공정조건 설정 등의 어려움에 직면하고 있다. 이러한 고감성 의류에 치명적인 문제를 유발하는 문제점에 관한 감성사 제조시의 공정조건 변화와 관련된 연구논문은 많이 발표가 되지 못하고 있다. 따라서 본 연구에서는 국내 7개 원사 Maker의 cake내의 Denier 별 PET 사의 물성을 균일한 길이의 Layer를 설정하여 분석, 조사하고 Layer 별 물성 차이와 습·건열 열처리 온도에 따른 사의 수축률 등을 비교함으로서 감성 의류용 직물 생산에 필요한 기초 물성 Data를 제공하고 PET 사의 품질향상을 도모함으로서 최종 감성 의류용 직물 소재 개발에 기여할 수 있는 기초자료를 제공하고자 한다.