Numerical simulations of the powder extrusion need an appropriate pressure-dependent constitutive model for densification modeling of the magnesium powders. The present research investigated the effect of representative powder yield function of the critical relative density model. We could obtain reasonable physical properties of pure magnesium powders using cold isostatic pressing. The proposed densification model was implemented into the finite element code. The finite element analysis was applied to simulation of powder extrusion of pure magnesium powder in order to investigate the densification and processing load at room temperature.

Aluminum alloys are not only lightweight materials, but also have excellent thermal conductivity, electrical conductivity and workability, hence, they are widely used in industry. It is important to control and enhance the densification behavior of metal powders of aluminum. Investigation on the extrusion processing combined with equal channel angular pressing for densification of aluminum powders was performed in order to develop a continuous production process. The continuous processing achieved high effective strain and full relative density at . Optimum processing conditions were suggested for good mechanical properties. The results of this simulation helped to understand the distribution of relative density and effective strain.

가변단면 압출기술은 사용하는 금형의 조합에 의해 다양한 가공이 가능한 성형공법으로, 압출시에 금형의 움직임에 의하여 제품의 단면형상을 변화시키거나, 치수와 두께를 동시에 변화시킬 수 있다. 압출공정에서 압출속도, 압출압력, 압출온도는 압출품의 표면결함이나 내부품질에 있어 중요한 영향인자이다. 그중 일정한 압출속도는 균일한 메탈 플로를 형성하여 성형품질에 있어서 고른 상태를 유지하게 만드는 요소이다. 기존의 압출 성형에서 펌프토출양의 변화에 의한 추출속도변동 문제는 램 속도의 변화를 계측하고 토출 양을 조정함으로써 압출속도를 제어하는 방법으로 해결한다. 그러나 가변단면 압출공정에서는 제품의 단면형상의 변화에 따라 압출비가 변하므로 이에 따른 램 속도 제어가 있어야만 한다. 본 연구에서는 가변단면 압출공정에서 가공형상에 따른 제어 알고리즘을 제시하여 가변 형상에 따른 램의 이동 속도 및 위치를 제공하려 한다.

The hypereutectic Al-20 wt%Si powders including some amount of Cu, Fe, Mg, Mn were prepared by a gas atomization process. In order to get highly densified Al-Si bulk specimens, the as-atomized and sieved powders were extruded at , Microstructure and tensile properties of the extruded Al-Si alloys were investigated in this study. Relative density of the extruded samples was over 98%. Ultimate tensile strength (UTS) in stress-strain curves of the extruded powders increased after T6 heat treatments. Elongation of the samples was also increased from 1.4% to 3.2%. The fracture surfaces of the tested pieces showed a fine microstructure and the average grain size was about

This work is to report not only the effect of rapid solidification of alloys on the micro-structure, but also the extrusion behavior on the materials properties. The average grain size of the atomized powders was about . The alloy powders of , consisted of I-Phase (Icosahedral, ) as well as Cubic structured W-Phase (), which was finely distributed within matrix. The oxide layer formed along the Mg surface was about 48 nm in thickness. In order to study the consolidation behavior of Mg alloy powders, extrusion was carried out with the area reduction ratio of 10:1 to 20:1. As the ratio increased, fully deformed and homogeneous microstructure could be obtained, and the mechanical properties such as tensile strength and elongation were simultaneously increased.

본 연구에서 돼지 난포란에서 채취된 난모 세포들을 체외성숙 후 형태적으로 선별하거나 극체 방출란을 선별하여 활성화 처리 후 48시간째에 분할란을 선별할 때 배발달율이 어느정도 향상되는지를 검토하였다. 난모 세포를 48시간 성숙 배양 후 형태적 선별과 극체의 방출 유무를 검사하고, 선별된 난모 세포들을 시간 추가 배양한 후 7% ethanol로 활성화시키고 cytochalasin B에 5시간 노출 후 PZM-5 배 양액으로 7일간 배양하였으며, 배양 중

The microstructural and mechanical properties of Al-Si alloyed powder, prepared by gas atomization fallowed by hot extrusion, were studied by optical and scanning electron microscopies, hardness and wear testing. The gas atomized Al-Si alloy powder exhibited uniformly dispersed Si particles with particle size ranging from 5 to . The hot extruded Al-Si alloy shows the average Si particle size of less than . After heat-treatment, the average particle size was increased from 2 to . Also, mechanical properties of extruded Al-Si alloy powder were analyzed before and after heat-treatment. As expected from the microstructural analysis, the heat-treated samples resulted in a decrease in the hardness and wear resistance due to Si particle growth. The friction coefficient of heat-treated Al-Si alloyed powder showed higher value tough all sliding speed. This behavior would be due to abrasive wear mechanism. As sliding speed increases, friction coefficient and depth and width of wear track increase. No significant changes occurred in the wear track shape with increased sliding speed.

Chemically pure, hydride/dehydride titanium powders were cold pre-compacted then extruded at and under argon. The extrusions were 100% dense with a narrow band of surface porosity and equiaxed microstructure of similar magnitude to the starting material. The tensile properties of the bars were better than conventionally extruded CP titanium bar product. Outcomes from this study have assisted in the identification of a number of key characteristics important to the extrusion of titanium from pre-compacted CP titanium powders, allowing the elimination of canning and hot isostatic pressing (HIPping) of billets prior to extrusion as per conventional PM processes.

Two different commercial aluminium powder grades have been densified by direct hot extrusion. The extrusion temperature was 425 °C, with an extrusion ratio of 1:16. Prior to extrusion, some green compacts were pre-sintered (500 °C). The evolution of the extrusion load during the process and the hardness of the final products have been investigated. Additionally, microstructural characterization by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Electron Backscattered Diffraction (EBSD) was carried out. The obtained results evidence grain refinement. Additionally, inter-metallic precipitation, dynamic recovery and geometric dynamic recrystallization take place depending on some process variables, powder composition, heat treatment, strain ...

본 논문은 Contour Crafting(CC) 프로세스의 압출과 적층 단계에서 물질 흐름의 형태를 연구하기 위한 실험과 모델링을 보여준다. 특히, 실험재료로써 진흙을 이용한 압출과 적층 메커니즘을 이해하기 위하여 기초적인 유한성분분석(FEA)을 실행하였다. FEA 시뮬레이션을 이용한, CC의 성능에 있어서 압출구멍의 기하학적인 효과에 대한 분명하고 기본적인 이해를 하게 되었다. 네모난 형상이 원하는 외부 표면특성을 만드는 것뿐만 아니라, 그리고 층간에